POLYALKYLENE GLYCOL

Polyalkylene glycol is the only major class of synthetic lubricants that are water soluble, making them invaluable where elastomer compatibility and thermal stability are paramount at elevated temperatures.

Their unique chemical structure, derived from ethylene oxide, propylene oxide, and butylene oxide, imparts diamond-like performance to lubricants, ensuring exceptional lubrication for metal-on-metal applications within a wide temperature range.

Polyalkylene glycol stand out for their high oxygen content, resulting in exceptionally clean lubrication that prevents the buildup of tars and sludges, a significant advantage over petroleum-based products.

Synonyms: Polyethylene glycols (PEG), Polypropylene glycols (PPG), Polyethylene oxide (PEO), Polypropylene oxide (PPO), Polyglycol, Polyether glycol, Polyether, Polyglycol ether, Polymeric glycol

Polyalkylene glycol is a range of ethylene oxide and propylene oxide derivatives built off different initiators, giving a product family with a wide range of solubility and viscosity properties.

Polyalkylene glycol is versatile polymers widely used across a range of industries.

They have gained a reputation within the lubricants industry as a high-performance lubricant weighed down by the baggage of incompatibility with other hydrocarbon lubricants, paints and seals.

This reputation may be outdated, and a better understanding of the underlying chemistry of Polyalkylene glycol will help operators understand where they can and cannot be used.

Polyalkylene glycol is a type of polymer, classified as API group five base stocks.

They are synthesized using three key oxides: ethylene oxide, propylene oxide, and butylene oxide.

These oxides are the building blocks for downstream derivatives known as polymers.

In the lubricants industry, these polymers are commonly referred to as Polyalkylene glycol.

There is a well-established infrastructure for producing ethylene oxide and propylene oxide, which serve as precursors for Polyalkylene glycol.

These oxides are also utilized in other industries, such as fuel additives, personal care products, paints, coatings, and more.

In fact, ethylene oxide and propylene oxide derivatives are found in everyday cleaning products and even in polyurethane foam used for seating.

Butylene oxide is a niche oxide that few chemical companies produce.

When combined with Polyalkylene glycol, it results in a new variant called oil-soluble Polyalkylene glycol.

Butylene oxide has a unique chemical structure with four carbons, compared to ethylene oxide (two carbons) and propylene oxide (three carbons).

This additional carbon imparts diamond-like performance to lubricants, although Polyalkylene glycol may also come with a higher price tag.

Polyalkylene glycol is typically used where elastomer compatibility and thermal stability are required at elevated temperatures.

Provides great lubrication for metal-on-metal applications within the -40°C to 200°C operating conditions.

They are the only major class of synthetic lubricants that are water soluble.

Polyalkylene glycol is unique among synthetic lubricants because of their high oxygen content.

As lubricants, they are exceptionally clean, allowing use where petroleum products would build tars and sludges.

By varying their structure, one can vary their solubilities from water soluble to water insoluble.

They are the only lubricants available with water solubility.

A product of World War II, they quickly found uses where petroleum-based lubricants fail.

This chapter covers lubrication uses only; however, Polyalkylene glycol have many applications in addition to lubrication.

Polyalkylene glycol is unique among lubricants.

They can have almost any solubility characteristics, and they are the only water-soluble class of lubricants.

In addition, their cleanliness, especially their low tendency to form carbon deposits, is extremely important.

Polyalkylene glycol will continue to enjoy modest growth, unless a large market develops (e.g., in automotive engine lubricants).

The growth in chemical modification of existing structures is expected to continue.

Manufacture And Major Uses of Polyalkylene glycol:

Manufacturers:

In the United States, the largest producer of Polyalkylene glycol is Union Carbide Corporation.

Other producers include Dow, Olin, and Huntsman.

In Europe, the largest producer is Inspec, with ICI being almost as large.

In Asia, Nippon Oil and Fat is the largest producer.

Other Asian producers include Sanyo and Idemitsu.

Dow is the sole producer of butylene oxide polymers.

Inspec is the sole producer of the oil-soluble propylene oxide/a-olefin epoxide copolymers.

The polypropylene glycol dimethyl ethers are not available as base fluids.

Idemitsu uses them internally.

Major Uses:

Polyalkylene glycol have found use as petroleum lubricant replacements when the cost is justified by a performance advantage.

Polyalkylene glycol differ from petroleum lubricants of similar viscosity in the following respects:

1. Lower pour point

2. Higher viscosity index

3. Lower tendency to form tar and sludge

4. Increased solvency

5. Wider range of solubilities, including water solubility

6. Higher flash point

7. Lower vapor pressure

8. Lower ash and metals content

9. Possess cloud points

Comparison of Polyalkylene glycol with petroleum should be done case by case, since petroleum lubricants can be formulated many different ways.

Polyalkylene glycol owe their commercial existence to the ability to do what petroleum products cannot.

Changing from petroleum lubricants to Polyalkylene glycol can present special problems.

Machinery that has been used with petroleum often has wear grooves filled with carbonaceous material.

Because of the good solvency characteristics of Polyalkylene glycol, this carbonaceous material is often removed on changeover, revealing wear scars that had not been visible earlier.

This wear is then incorrectly attributed to the Polyalkylene glycol.

Petroleum-derived sludge can also be softened and result in clogged filters.

Although Polyalkylene glycol is compatible with most elastomers, this area should be evaluated before changeover.

Polycarbonate and polyurethane machine parts are sometimes softened or embrittled.

Polycarbonates are often used as site glasses on lubricant reservoirs.

The good solvency properties tend to result in softened and lifted paint.

In the case of exterior paint, this is a cosmetic issue.

Catalyzed epoxy, epoxy-phenolic, or modified phenolic coatings have performed well in contact with Polyalkylene glycol.

In the case of interior paint, the lifted coating can result in clogged filters and orifices if care is not taken during the conversion process.

Fire-Resistant Hydraulic Fluids:

Fire-resistant hydraulic fluids are used wherever fires cannot be tolerated.

Fire-resistant fluids are used in areas like foundries, die-cast aluminum facilities, steel mills, and mines.

The traditional classes of fire-resistant hydraulic fluids are the Polyalkylene glycol based water glycol fluids, oil-in-water emulsions, phosphate esters, and polyol esters.

Fire-resistant hydraulic fluids can be formulated from Polyalkylene glycol.

These are the so-called water–glycol fluids.

Fire resistance of hydraulic fluids is measured by standard tests.

The most widely used of these are the spray flammability test and the hot channel test, industry standard tests run by Factory Mutual Corporation.

In the spray flammability test, an aerosol of the test fluid is sprayed through a flame.

The following results are obtained:

Petroleum-based hydraulic fluids burned with a large flame while the oil was being sprayed.

Combustion continued after the ignition source was removed.

Both polyol ester and phosphate ester burned while being sprayed through the ignition source.

The burning stopped when the ignition source was removed.

This is considered to be a passing result.

Water/glycol fluids did not burn when sprayed through the ignition source.

In the hot channel test, hydraulic fluid is sprayed onto a steel channel heated to 7048C and inclined at 30 degrees.

This test is used to evaluate spillage of the test fluid onto a heated surface.

The various classes of lubricants have the following results:

The petroleum-based hydraulic fluid burned with a very large flame.

The phosphate ester did not burn with a flame, but did emit large volumes of white smoke.

The polyol ester burned like the oil while being sprayed, but the burning stopped when the spray stopped.

The water/glycol fluid burned with a reduced flame.

Both the polyol ester and the phosphate ester passed me test, which calls for the fluid to stop burning 5 seconds after the spray of hydraulic fluid stops.

They still exhibit fire-related risks (smoke, flames), which are greatly reduced in the case of the water/glycol fluid.

Part of the reason for the superior fire resistance of water/glycol fluids lies in the lower heat content of the fluids.

Not only do the water/glycol fluids have to evaporate water until the organic portion is left, but the organic portion consists of materials that have lower heat values because of their polyether structures.

Essentially, the polyether structure means that such a compound is already partially burned.

Water-in-oil emulsions, with water contents of 80%, show fire-resistant performance most similar to that of water/glycol fluids.

They are lower in viscosity, and as a result should be used in pumps with narrower tolerances, requiring the use of better filtration to prevent particles from damaging the moving parts.

The lower viscosity also leads to higher pump wear.

Because they have water contents as high as 80%, their upper temperature limit of use is 608C owing to the vapor pressure of the contained water.

They are prone to microbial degradation, and use of biocides in the machinery should be considered.

These tests were run according to a German standard (DIN 51, 389 E) using a Vickers V-104C vane pump for 250 hours at 1500 psi and 1500 rpm.

Because of their high water content water/glycol fluids have been traditionally limited to about 2000 psi operating pressure.

Recently, high performance water/glycol fluids have been developed.

These fluids can operate at pressures at least 5000 psi.

In addition to higher pressures and excellent fire resistance, the fluids show low wear rates as well.

These tests were run according to ASTM D-2882 for a duration of 100 hours at 2000 psi and 1200 rpm using a Vickers V-104 vane pump.

The pass test criterion is 1 mg/h wear rate.

Water/glycol fluids show Newtonian behavior.

They do not thin out with shearing, which can reach 106 s21 in hydraulic pumps.

BASF tried to market a higher water content fluid using a novel Polyalkylene glycol based thickener.

The Polyalkylene glycol contained a hydrophobic end group that resulted in associative thickening in the aqueous environment.

These fluids suffered from excessive shear thinning and high pump wear.

Water/glycol-based hydraulic fluids thickened with Polyalkylene glycol are formulated in the viscosity region of low to medium viscosity oils.

Their use temperature is limited from about 230 to 658C.

The upper temperature limit is a result of the high vapor pressure of the contained water.

Higher temperatures can lead to cavitation and premature pump failure.

These fluids generally have good seal compatibility.

To achieve optimal performance of water/glycol fluids, proper maintenance is essential.

Water content must be controlled to the specification level.

Too little water will significantly raise the viscosity.

Too much water will thin viscosity and also result in significant increases in wear.

Water content is easily measured by refractometry.

The amine, or alkalinity, content must also be monitored.

Higher wear can be experienced if the alkalinity is above the desired value.

Greater wear will result if alkalinity is below the desired value.

Alkalinity is easily monitored through acid–base titrations.

The maintenance problems with phosphate esters are different.

The phosphate esters are the only widely used nonaqueous fluids employed as fire-resistant hydraulic fluids.

These are triaryl and trialkyl esters of phosphoric acid.

Like all esters, they are subject to hydrolysis back to their parent acid.

Hydrolysis rate depends on structure, with the longer alkyl chain esters being the most resistant.

They are frequently used with a bleaching clay filter to remove the acidic hydrolysis and oxidation by-products.

Brake Fluids:

The use of Polyalkylene glycol as the hydraulic fluid in braking systems for motor vehicles was one of the early uses of Polyalkylene glycol.

The properties that made them valuable were water miscibility, low pour point, high viscosity index, high boiling point, good elastomer compatibility, and low vapor pressure.

Glycol ethers are commonly added, as are rust inhibitors and antioxidants.

The ability to absorb water is the property most useful in this application.

At low temperatures, ice crystals would prevent the operation of the breaking system.

At high temperatures, water could vaporize, causing “vapor lock.”

Even with the tendency to absorb water, the vapor lock temperature drops by about 808C when the anhydrous system picks up 2% water.

Water increase at low temperature increases the viscosity of the fluid.

The lower the temperature, the greater the effect.

This effect is due to hydrogen bonding, which is a weak interaction favored at reduced temperatures.

Silicone brake fluids are the only significant alternative to the Polyalkylene glycol fluids.

They have been utilized for their greater temperature stability in the newer generation of cars that have higher under-the-hood and brake operating temperatures.

Their main disadvantages are higher cost and a water tolerance below that of the Polyalkylene glycol based fluids.

The two types of brake fluids are mutually insoluble, and Polyalkylene glycol is important not to mix them.

If the two types are mixed, the additives tend to partition between the two phases so that neither phase is properly protected against corrosion.

Brake failure can result.

Compressor Lubricants:

The compression of petroleum-derived gases such as methane, ethane, and ethylene presents a severe lubrication challenge.

These process gases dissolve in petroleum and petroleum-like lubricants, serving to reduce the viscosity of the lubricant.

As a result, very viscous petroleum oils are used, to induce the process gas to thin the lubricant to the desired viscosity at the use temperature.

Unfortunately, this makes start-up, especially under cold conditions, very difficult.

In addition, if the process gas contains higher petroleum fractions that reach their dewpoint when compressed, droplets will form that will wash the cylinder wall, leaving Polyalkylene glycol essentially unlubricated.

Compared to other lubricants, hydrocarbon gases have greatly reduced solubility in the watersoluble Polyalkylene glycol.

Other process gases that have been used successfully include hydrogen, carbon dioxide, landfill gas, and propane.

Common benefits are reduced wear, cleaner systems, reduced maintenance, and reduced lubrication rates.

A few manufacturers market Polyalkylene glycol based air compressor lubricants.

This use depends on additive technology to limit air oxidation, is primarily limited to petroleum products.

Textile Lubricants:

Water-soluble Polyalkylene glycol is widely used in the textile industry.

They are nonstaining and can be washed from the finished yarn or fabric with water.

Polyalkylene glycol, when they are oxidized at moderate temperature with an adequate oxygen supply, do not form colored by-products.

This property is particularly advantageous in the textile industry, where color is a critical quality consideration.

The same property that makes Polyalkylene glycol useful as lubricants for fibers makes them important machine lubricants in the textile industry.

If they come into contact with the textiles being worked, they are easily washed off.

However, they tend to cause crazing of polycarbonate sight glasses.

Calender Lubricants:

Petroleum meets the need of lubricating the large-diameter journal bearings, antifriction bearings, and gears that are present in mills and calenders used by the rubber, textile, paper, and plastics industry up to temperatures of 3508F.

Above 3508F, petroleum products tend to form sludges, calling for increased maintenance.

Polyalkylene glycol have been used in this application, since they do not tend to form sludge or carbon deposits.

Metalworking Fluids:

Polyalkylene glycol is often used as lubricity additives in water-based cutting and grinding fluids.

In addition, they have been utilized in drawing, forming, stamping, and rolling lubricants.

Because of their good water solubility, Polyalkylene glycol is most often used in “synthetic” metalworking fluids.

These fluids form true solutions in water.

Synthetic metalworking fluids based on Polyalkylene glycol provide good lubricity and are excellent coolants.

In general, they are also more resistant to microbial attack and easier to maintain that “soluble oil” metalworking fluids, which are actually oil-in-water emulsions.

Polyalkylene glycol provide good lubricity in synthetic metalworking fluids by taking advantage of their inverse solubility in water.

At ambient temperatures, Polyalkylene glycol is water soluble.

At an elevated temperature, known as the “cloud point,” the Polyalkylene glycol becomes insoluble and forms small polymer droplets.

When a synthetic metalworking fluid containing a Polyalkylene glycol is brought into contact with a hot die or cutting tool, Polyalkylene glycol is heated to a temperature above the cloud point of the polymer.

The Polyalkylene glycol then comes out of solution.

The resulting Polyalkylene glycol droplets coat the surfaces of the hot die or cutting tool, forming a lubricant film that provides excellent hydrodynamic lubricity.

Synthetic metalworking fluid formulations often contain both Polyalkylene glycol and water-soluble boundary or extreme pressure additives such as fatty acids or phosphate esters.

Combinations of Polyalkylene glycol and fatty acids or phosphate esters have been shown to be synergistic, providing better lubricity than equivalent concentrations of either additive by itself.

As a result of this synergy, these aqueous metalworking fluids provide excellent lubricity as well as the good cooling properties of water.

Synthetic metalworking fluids will also contain other additives such as corrosion inhibitors, antifoams, and biocides.

Refrigeration Lubricants:

A major new application for Polyalkylene glycol (PAG) lubricants is in vehicle air conditioning (A/C) systems.

All new air-conditioned cars and trucks sold in North America contain refrigerant R-134a and Polyalkylene glycol lubricants in their A/C systems.

All major car makers are also recommending Polyalkylene glycol lubricants for the retrofitting of vehicles from refrigerant R-12 to R-134a.

In 1987 the Montreal Protocol initiated a program to phase out the production and use of chlorofluorocarbons (CFCs) because of their adverse effect on the earth’s ozone layer.

A major use of chlorofluorocarbon R-12 was as a refrigerant in mobile air conditioning systems.

Refrigerant R-134a was chosen by this industry as a non-ozone-depleting replacement for R-12.

In mobile A/C systems, the compressor lubricant travels through the system with the refrigerant.

To ensure return to the compressor, the lubricant must have adequate solubility in the refrigerant.

The mineral oils that are used as lubricants with R-12 are insoluble in R134a.

Polyalkylene glycol lubricants show good solubility in R-134a.

Because of their good solubility and lubricating characteristics, Polyalkylene glycol lubricants have been chosen by the automotive industry for use in R-134a A/C systems.

Polyalkylene glycol have a number of physical properties that enable them to perform well as refrigeration lubricants when used in conjunction with R-134a.

These include their good solubility and stability in R-134a, excellent lubricity, and compatibility with many common elastomers.

The good low temperature flow properties and low volatility of Polyalkylene glycol is also important in refrigeration applications.

While Polyalkylene glycol have a number of physical properties that are desirable in a refrigeration lubricant, Polyalkylene glycol is their good solubility in R-134a that has led to their use in mobile A/C systems.

Polyalkylene glycol refrigeration lubricants exhibit excellent low temperature solubility.

They also show a high temperature insolubility region at low Polyalkylene glycol concentrations.

In general, the lower the viscosity of the PAG, the better the high temperature solubility.

In the high temperature insolubility region the R-134a/Polyalkylene glycol mixture will separate into two layers.

These two layers are not pure refrigerant and pure lubricant, but instead consist of a lubricant-rich phase and a refrigerant-rich phase.

The composition of the two phases that form in the high temperature insolubility region can be determined from the intersection of the horizontal temperature tie line with the PAG’s solubility curve.

The excellent low temperature miscibility of Polyalkylene glycol and R-134a, as well as their mutual solubility at elevated temperatures, ensures the circulation of lubricant through the A/C system that is necessary for good compressor lubrication.

While lubricant solubility in the refrigerant is necessary, Polyalkylene glycol is also important for the refrigerant/lubricant pair to be chemically and thermally stable.

Polyalkylene glycol lubricants exhibit excellent stability in R-134a.

Sealed-tube stability tests run at 3508F (1758C) for 14 days in the presence of steel, aluminum, and copper coupons show the PAG/R-134a combination to be at least as stable as mineral oils run under the same conditions in the presence of R-12.

Polyalkylene glycol is excellent lubricants.

Of particular importance in refrigeration applications are the high viscosity indices of Polyalkylene glycol, typically ranging from 180 to over 250.

Polyalkylene glycol refrigeration lubricants thus show significantly less change in viscosity with temperature than do mineral oils, whose viscosity indices are typically less than 100.

This means that compared to mineral oils, Polyalkylene glycol is more fluid at low evaporator temperatures and still provide good lubricity in the hot compressor.

Polyalkylene glycol is compatible with most common elastomers.

However, Polyalkylene glycol is important to consider the effect of the R-134a when both the refrigerant and lubricant are present.

Because of the variations that can exist between elastomers in the same generic family, Polyalkylene glycol is important to test the compatibility of the refrigerant/lubricant pair with the specific elastomers that are to be used in critical applications.

One of the major differences between Polyalkylene glycol and mineral oils is their affinity for water.

Polyalkylene glycol is hygroscopic relative to mineral oil lubricants.

Polyalkylene glycol refrigeration lubricants usually have a maximum water specification of 1000 ppm and normally contain between 400 and 800 ppm water.

Because they are hygroscopic, Polyalkylene glycol will pick up water when exposed to humid air.

They will continue to pick up water until an equilibrium or saturation level is achieved.

Typical saturation levels range from 1 to 5%, depending on the humidity and the structure of the PAG.

Polyalkylene glycol is important to realize that the water absorbed by Polyalkylene glycol is not free but is instead bound to the Polyalkylene glycol backbone.

Therefore neither corrosion nor ice crystal formation has been a problem in automotive A/C systems that are lubricated with Polyalkylene glycol.

Because of their hygroscopicity, Polyalkylene glycol refrigeration lubricants should not be exposed to humid air during storage.

Bulk storage tanks and drums should be nitrogen blanketed or equipped with vent dryers.

For storage in small containers, minimizing air exposure is usually sufficient to keep Polyalkylene glycol refrigeration lubricants in satisfactory condition.

There have been many questions asked regarding the proper handling of Polyalkylene glycol.

Polyalkylene glycol refrigeration lubricants are significantly less hygroscopic than brake fluids meeting U.S. Department of Transportation Standards (DOT-3).

If the same care is taken when Polyalkylene glycol lubricants are handled that is exercised in work with DOT-3 brake fluids, no performance problems should occur.

Proper handling consists simply of keeping the lubricant container closed when not in use, and minimizing the amount of time the lubricant is exposed to the air during its transfer from the container to the A/C system.

Any water that is introduced into an A/C system with the Polyalkylene glycol will be removed by the molecular sieve dryer.

A challenge currently facing the automotive industry is how to service the R-12 vehicles on the road today as the supply of this refrigerant becomes scarce.

Much work has been done in the automotive industry to determine the best ways to convert, or retrofit, these R-12 vehicles to R-134a.

A retrofit lubricant must be compatible with residual R-12 and mineral oil as well as soluble in R-134a.

Compressor makers, car manufacturers, and component suppliers have evaluated the use of Polyalkylene glycol as retrofit lubricants.

Polyalkylene glycol have performed very well in these evaluations, and all major car companies have chosen Polyalkylene glycol lubricants for use in the retrofitting of their vehicles.

One of the major requirements of a retrofit lubricant is stability in the presence of residual R-12.

Analysis of the refrigerant in retrofit vehicles shows that the residual concentration of R-12 is typically about 1%.

A worst-case retrofit would leave approximately 5% R-12 in the A/C system.

Because of the ease with which the R-12 concentration can be reduced to low levels, concerns about contamination of the refrigerant supply, and the higher pressures exerted by R-12/R-134a mixtures, the Society of Automotive Engineers has declared that the concentration of R-12 must be reduced to below 2%.

High temperature and long-term sealed-tube tests show that Polyalkylene glycol refrigeration lubricants are stable in the residual R-12 concentrations that can be expected in retrofit vehicles.

Also, the analysis of lubricant samples from retrofit tests on compressor stands and from actual retrofit vehicles has shown no signs of Polyalkylene glycol or R-134a degradation.

Polyalkylene glycol is compatible with used mineral oils in that they do not undergo any adverse physical or chemical reactions when they are mixed.

Some Polyalkylene glycol exhibit limited solubility in mineral oils, but their performance in retrofit applications is not adversely affected.

Polyalkylene glycol lubricants have been used in retrofit trials where 50–100% of the original mineral oil charge was left in the A/C system.

In most of these trials, no lubricant-related problems were experienced.

The lubricant problems that did occur were due to lubricant slugging and subsequent compressor failure.

Slugging is not caused by incompatibility between the Polyalkylene glycol and mineral oil; rather, Polyalkylene glycol is the result of too much lubricant in the system.

Therefore, removing as much mineral oil as practical is generally recommended when a vehicle is being retrofitted from R-12 to R-134a.

Since Polyalkylene glycol lubricants are compatible with residual R-12 and mineral oil, much work was done by the automotive industry to show that Polyalkylene glycol is good retrofit lubricants.

Many different retrofit scenarios using R-134a and Polyalkylene glycol lubricants were evaluated in an effort to determine the most costeffective method for a given A/C system.

In general, the performance of the Polyalkylene glycol lubricants in these retrofit tests has been excellent.

They provide good lubricity and have proven to be compatible with residual R-12 and mineral oil.

All major car manufacturers have decided to retrofit their vehicles with R-134a and Polyalkylene glycol lubricants.

To achieve a reliable, cost-efficient retrofit, however, different procedures are recommended for different vehicles.

When retrofitting a vehicle from refrigerant R-12 to R-134a, Polyalkylene glycol is important to follow the car maker’s specific recommendations.

Two-Cycle Engine Lubricants:

Polyalkylene glycol based on polypropylene glycol were recognized as lubricants for use with air cooled two-cycle engines as early as 1946.

The excellent lubricating properties of Polyalkylene glycol based two-cycle lubricants have been demonstrated over the years in competition Moto-cross and Enduro racing.

Freedom from plug fouling due to carbonaceous residues has been demonstrated repeatedly on test stands as well as in trail and street riding.

Polyalkylene glycol lubricants are also used as lubricants in high performance engine fuels for gocarts and model engines.

Polyalkylene glycol show good solubility in gasoline as well as methanol and nitromethane-methanol mixtures.

They provide good lubricity and excellent detergency.

The clean burn-off properties of Polyalkylene glycol based two-cycle engine lubricants virtually eliminate engine problems related to spark plug fouling, combustion chamber deposits, and exhaust port plugging.

Recently Southwest Research performed Japanese Automobile Standards Organization (JASO) tests on a Polyalkylene glycol two-cycle engine lubricant.

The Polyalkylene glycol-based product demonstrated excellent performance compared to a high quality petroleum oil based standard.

Four JASO tests were used to measure the following key two-cycle engine lubricant properties: lubricity and torque, detergency, smoke, and exhaust system blocking.

In all four cases a high quality petroleum oil based product, JATRE 1, was used as a reference.

A test result of 100 shows that the test lubricant performed as well as JATRE 1.

A value of less than 100 means that the test lubricant did not perform as well as JATRE 1, while a value of greater than 100 indicates that the Polyalkylene glycol lubricant outperformed the reference oil.

JASO has three classifications of two-cycle engine lubricants.

These categories are FA, FB, and FC, with FC being the most demanding.

A Global Specification performance index has been proposed by the International Organization for Standardization (ISO).

The ISO classifications are GB, GC, and GD, with GD representing the best rating.

Crankcase Lubricants:

The use of Polyalkylene glycol as passenger car motor oils was pursued in the mid-1940s.

These synthetic lubricants, based on polypropylene glycol monobutyl ethers, were evaluated in engine test stands and in extensive vehicle trials.

The very high viscosity indices and inherent good lubricity of these products resulted in wear of engine parts comparable to that of the best petroleum oils of the time.

The Polyalkylene glycol lubricants demonstrated a number of advantages relative to petroleum-based motor oils.

These included less sludge formation, reduced combustion chamber deposits and spark plug fouling, excellent detergency, and better low temperature properties.

However, distribution problems, poor compatibility with conventional petroleum oils, and high cost prevented Polyalkylene glycol based automotive crankcase lubricants from being commercially successful.

Work is continually being done to improve the performance properties of engine lubricants.

Higher viscosity indices are needed to provide good low temperature flow properties while retaining sufficient lubricity at the high temperatures that exist in today’s engines.

Good detergency reduces sludge formation.

Better engine efficiencies, reduced emissions, and lower maintenance can be achieved by reducing the deposit-forming tendencies on intake valves and in the combustion chamber.

These requirements have led to renewed interest in the use of Polyalkylene glycol as engine crankcase lubricants because of their high viscosity indices, good detergency, and clean burn-off characteristics.

Oil-soluble Polyalkylene glycol have recently been developed that solve the oil compatibility problems associated with conventional Polyalkylene glycol while retaining the performance advantages provided by this class of synthetic lubricants.

These new Polyalkylene glycol is made from the copolymerization of propylene oxide and an a-olefin epoxide onto a lipophilic alcohol starter.

Engine trials and other motor oil evaluation tests showed that multigrade synthetic and semisynthetic lubricants containing these oil-soluble Polyalkylene glycol provided the benefits expected from similar formulations containing esters and poly(a-olefins).

In addition, the formulations containing the oil soluble Polyalkylene glycol required less viscosity index improver and showed reduced volatility and improved engine cleanliness.

Market Size of Polyalkylene glycol:

Worldwide production of Polyalkylene glycol for lubrication use is approximately 100 million pounds.

The U.S. market represents about 50 million pounds.

The polyalkylene markets for other uses, such as components in urethane foams or surfactants, dwarfs the use for products manufactured for lubrication purposes.

In addition, the Polyalkylene glycol manufactured for lubrication have other uses, such as heat transfer fluids, solder assist fluids, and metal quenchants, that are not included in the preceding estimates.

End Group Chemistry of Polyalkylene glycol:

The Polyalkylene glycol all have at least one hydroxyl group on the end of the molecule.

If they have been produced from water or a multifunctional starter, they will have more than one hydroxyl group.

The polyols used for urethane applications perform by virtue of the reaction of the hydroxyl groups reacting with isocyanate groups to give the urethane linkage.

In this application, stearic factors cause the primary hydroxyl group to be more reactive than a secondary hydroxyl.

The urethane polyols are formed from propylene oxide.

Since this results in a less reactive secondary hydroxyl end group, Polyalkylene glycol is necessary to end-cap the polyol with a small amount of ethylene oxide to increase the number of primary alcohol terminated molecules.

Other end group reactions are used to functionalize Polyalkylene glycol.

These reactions use the known alcohol derivatization reactions.

Esters are formed by reaction with either organic or inorganic acids.

In addition to the etherification reactions already discussed, Polyalkylene glycol is possible to react the alcohol with a strong acid and an olefin to give an alkyl ether cap.

Other derivatization reactions of the alcohol end group are possible.

Polyalkylene glycol has been reported that poly (dichlorophosphazene) can be reacted with Polyalkylene glycol to give poly(phosphazene) derivatized with grafted Polyalkylene glycol chains.

These materials are reported to have utility as metalworking lubricants.

Coordination Chemistry of Polyalkylene glycol:

The presence of an ether oxygen atom at every third position of the polymer backbone leads to the rich coordination chemistry of these compounds.

The use of these polymers as phase transfer agents has been reviewed.

Complexation with phenols, phenolic resins, bromine,iodine, gelatin, sulfonic acids, mercuric slats, tannic acid, poly(acrylic acid), and urea all have been reported.

The use of poly(ethylene oxide) polymers as flocculation agents is related to their absorption on colloidal silica, clay, and minerals.

The facile wetting of metal parts in lubrication applications is related to the ability of the polymer to associate with me metal surface.

Like the complexation of other chemical species, the ability of the Polyalkylene glycol to wet a metal surface is due to the presence of an ether oxygen atom at every third position of the polymer chain.

This results in good extreme pressure and metalworking performance.

The solution properties of these polymers in water are also directly related to the association of the water with the ether oxygen atoms.

Oxidative and Thermal Stability of Polyalkylene glycol:

The bond strength of the carbon–carbon bond is 84 kcal/mol (ethane), which is slightly stronger than the 76 kcal/mol carbon–oxygen bond of an ether (dimethyl ether).

Other authors have reported that carbon–oxygen ether bonds are comparable to, or slightly stronger than, the usual carbon–carbon bonds.

However, from a thermochemical standpoint, Polyalkylene glycol is usually considered less stable than typical hydrocarbons.

In the absence of air, they can be used up to about 2508C.

The poly(alkylene oxides) are all polyethers with an oxygen atom in every third position of the polymer backbone.

As with all ethers, a secondary or tertiary carbon adjacent to the ether oxygen is susceptible to oxidative attack.

The mechanism involves a free radical abstraction of the hydrogen on the a carbon, resulting in a carbon-based radical stabilized by the adjacent oxygen atom.

This can then react with oxygen to produce a peroxy radical.

The process does not continue to build peroxide levels, since a number of mechanisms lead to peroxide destruction.

In the early stages of oxidation the peroxide will increase, but as the reaction proceeds and carbonyl levels build, the peroxide level reaches a steady state.

Further reaction will lead to the formation of acidic material.

As the acidic oxidation products build, the viscosity begins to drop.

Studies of the oxidation of polypropylene glycols and polyethylene glycols show that the polymers degrade into lower molecular weight products as they oxidize.

This is in contrast to the behavior of petroleum products, which build higher molecular weight products as they oxidize.

Polyalkylene glycol is these higher molecular weight materials that precipitate from the oil and produce sludge.

Polyalkylene glycol is the fate of the hydroperoxides that determines the tendency of a lubricant to form sludge.

In the case of petroleum, the hydroperoxides form hydrocarbon-based aldehydes, which can undergo aldol condensations to form high molecular weight a,b-unsaturated species that themselves are reactive.

This leads to the formation of high molecular weight polar species that are not soluble in the parent nonpolar base oil and therefore precipitate out of solution to form sludge.

The fate of hydroperoxides is different in Polyalkylene glycol and in petroleum.

Because every third atom is an oxygen, a high proportion of the chain cleavage products in the former case are esters.

While esters can condense, the reaction is difficult and is unlikely to occur.

The type of end groups can be determined by proton magnetic resonance.

In the case of polypropylene glycols, the reaction products are more complex owing to the greater complexity of the molecules.

These end groups are not simple aldehydes and will undergo condensation with difficulty.

When sufficient degradation has taken place, volatile products will be produced.

The oxidation of Polyalkylene glycol yields polar, oxygenated products.

Polyalkylene glycol themselves are polar and will dissolve these oxidation products.

In contrast, oils are nonpolar and their oxidation products are polar, consisting of peroxides and carbonyl species as well.

Oils will not dissolve these polar species, and this property contributes directly to their tendency to form sludge and varnish.

The tendency of Polyalkylene glycol to solubilize their own degradation products, and their cleavage to form volatile species, can be cited to explain their low Conradson carbon and Ramsbotton carbon (ASTM D189 and D 524), typically less that 0.01%.

When sludges do form from Polyalkylene glycol, Polyalkylene glycol is usually in oxygen-starved systems as a result of aldehyde condensation.

Under conditions of exhaustive oxidation, the chain cleavage will have occurred to such an extent that the oxidation products evaporate.

The volatilization of the fluid, together with the tendency not to form carbon or sludge, means that the Polyalkylene glycol will be removed under high temperature applications in a property known as clean burn-off.

Clean burn-off is important in a number of the applications for these products—for example, as a carrier for graphite on chains being used in ovens or kilns.

As with the pyrolysis products of any organic material, good ventilation, should be installed to ensure the removal of the vapors from the workplace.

The oxidation of Polyalkylene glycol could result in shorter than desired service life for some applications.

Oxidation can effectively be controlled through the addition of antioxidants to interrupt the chain transfer oxidation mechanism.

Typical antioxidants that have been used include butylated hydroxyanisole, phenothiazine, hydroquinone monomethyl ether, butylated hydroxytoluene, and phenyl-a-naphthylamine.

The poly(alkylene oxides) are dramatically stabilized toward oxidation by the addition of antioxidants.

In many cases antioxidants at levels of a few hundred parts per million are sufficient to stabilize against oxidative degradation under mild conditions and higher levels will stabilize these systems under much more severe conditions.

The uses of inhibited Polyalkylene glycol as heat transfer fluids and as gear and calender lubricants are all examples of successful high temperature applications.

These applications show that if the system is protected against oxidative attack, either by the addition of an antioxidant or by removal of oxygen, Polyalkylene glycol will have very good high temperature stability.

Physical Properties of Polyalkylene glycol:

Base Fluids:

The physical properties of poly(alkylene oxides) are best understood by considering them as a series of homologous derivatives.

Thus the polymers derived exclusively from ethylene oxide are considered as members of one class differing primarily in molecular weight.

The trends in properties can then be understood in relationship to structure.

As these data indicate, the poly(alkylene oxides) with a molecular weight above about 600 are crystalline solids.

The alcohol-started products follow the same pattern.

The structure in the solid state has been examined by infrared, x-ray diffraction, and Raman spectroscopy.

Polyalkylene glycol has been concluded that the molecules exist in a helical structure.

The high symmetry of the structure leads to high crystal packing energies that favor crystallization.

Although polyethylene glycols (PEGs) are soluble in water in all proportions, the phase of the solution may be solid or liquid.

For instance, PEG-8000 will form a homogeneous liquid with water in all proportions above its melting point, but if the concentration of PEG-8000 is above 50%, the solution will freeze or become a paste at room temperature.

These are derived from a butyl alcohol starter.

In contrast to the polymers of poly(ethylene oxide), these polymers do not readily crystallize.

Instead, they become too thick to flow at a temperature known as the pour point.

The pour point for these polymers is very low.

Even at temperatures below their pour point they do not crystallize but form a glasslike solid.

The pendant methyl group on the backbone breaks up the crystal packing.

These polymers have very high viscosity indices.

The monobutyl ethers polymers are derived from a butyl starter and are formed from equal weights of ethylene oxide and propylene oxide.

The diol polymers are derived from water, giving them two hydroxyl groups.

The oxide incorporated in these is 75 wt % ethylene oxide and 25 wt % propylene oxide.

The copolymers derived from equal amounts of ethylene oxide and propylene oxide have very low pour points.

If we compare the pour points of these random copolymers with those of the polymers derived from propylene oxide, we find the values very similar.

In fact, the copolymers seem to have slightly lower pour points at the higher molecular weights.

This may be due to the slightly higher symmetry of the homopolymers of propylene oxide compared to the mixed copolymers.

These copolymers have even higher viscosity indices than was the case with the polymers derived only from propylene oxide.

The random copolymers derived from block feeds of ethylene oxide and propylene oxide have physical properties that are dependent on the relative size of each block as well as the total molecular weight.

Commercially available products are derived from poly(propylene glycol), which is then reacted with ethylene oxide.

Alternatively, a poly(ethylene glycol) molecule can be reacted with propylene to produce what is referred to as a reverse blocked structure.

These products are available as liquids, pastes, or flakable solids.

Butylene oxide polymers are available as either diols or monobutyl ethers.

In general, the butylene oxide monobutyl ethers have lower viscosities and lower viscosity indices compared to the same molecular weight ethylene oxide/propylene oxide (EO/PO) copolymer or propylene oxide polymer.

This is to be expected, since the polymer chains are not as long (fewer repeating units) for the same molecular weight.

Intermediate viscosity grades are available by blending these two fluids A typical polypropylene glycol dimethyl ether used for lubrication has properties shown in Table 8.

Viscosity index, the measure of the change in viscosity with temperature, is very much dependent on polymer structure.

In linear polymers, which comprise the major base fluids used in lubrication, the viscosity index depends on the end groups and on which oxides are used in synthesis.

This effect is almost certainly due to hydrogen bonding among the hydroxyl groups at low temperature.

This weak effect, which will serve to make the effective molecular weight seem larger and the polymer more viscous, will be broken up with the addition of thermal energy.

Thus we see that Polyalkylene glycol takes a smaller molecule to achieve a target viscosity at low temperature if that molecule has hydroxyl groups.

For fluids isoviscous at 1008C, the viscosity index decreases as the number of carbon atoms in the epoxide monomers increases.

Thus, substituting propylene oxide for ethylene oxide decreases the viscosity index, as will substituting butylene oxide for propylene oxide.

Although the molecular weights are not given in the preceding examples, for the EO/PO copolymers, isoviscous polymers at 408C have the same molecular weight whether they are polypropylene glycol monobutyl ethers or EO/PO monobutyl ether copolymers.

This means that the polypropylene glycol monobutyl ether molecule is shorter.

Shorter molecules cannot unfold as far at increased temperature, giving a lower degree of chain entanglement and viscosity.

The film-forming properties of lubricants are critical.

Under extreme pressure, lubricating materials tend to thicken.

This behavior is important in keeping a liquid layer between the parts being lubricated.

Yet, tests under boundary lubrication conditions showed that improved friction and wear behavior was found in EO/PO polymers as the amount of EO was increased.

In all cases, with or without additives, the Polyalkylene glycol outperformed the petroleum test fluids.

All polyethers tested reached load levels of 10 or more without EP additives in the FZG test, promulgated by the German standard-making body.

Other workers report load levels of 12 with Polyalkylene glycol in the FZG gear test (A/16, 6/140).

Polyalkylene glycol may be that the pressure–viscosity coefficient is important only in extreme pressure applications, such as heavily loaded ball bearings.

Under less stressful applications, such as gears, the increased polarity provided by ethyloxy groups will allow greater interaction with the polar metal oxides that exist on metal surfaces.

This may give the molecules their mild extreme pressure additive qualities.

Solution Properties:

The aqueous solution properties of Polyalkylene glycol is critical for many of their commercial applications.

Polyalkylene glycol show the property of inverse solubility.

In other words, their solubility in water decreases as the solution temperature rises.

At a temperature known as the cloud point, the Polyalkylene glycol comes out of solution and forms a turbid, or cloudy, dispersion.

For copolymers of ethylene oxide and propylene oxide and the propylene oxide homopolymers, the cloud point is a function of molecular weight and the proportion of ethylene oxide used in the synthesis.

Increasing the molecular weight in an otherwise similar Polyalkylene glycol series lowers the cloud point.

Raising the amount of ethylene oxide relative to propylene oxide in the synthesis of Polyalkylene glycol of otherwise similar structure raises the cloud point.

Cloud point is very sensitive to salt concentration, which lowers the cloud point.

The cloud point is generally below room temperature for the homopolymers of propylene oxide.

They are generally not considered soluble in water, although the lower molecular weight examples are readily dissolved in cold water.

The cloud points for common Polyalkylene glycol is shown in Fig. 1.

Butylene oxide polymers will have a greater degree of water insolubility than the propylene oxide polymers because of their decreased oxygen content.

The cloud point is an important property in metalworking applications.

Water-based metal working fluids often contain 1–5% Polyalkylene glycol.

When the polymer is exposed to the high temperature of the working surface, Polyalkylene glycol comes out of solution to provide the lubricity needed.

The hydration of Polyalkylene glycol in aqueous solutions has been examined by differential scanning calorimetry.

The more water-soluble poly(ethylene oxide) polymers were found to coordinate 2.8 moles of water per ether linkage, while the copolymers derived from equal weights of ethylene oxide and propylene oxide coordinated to 2.4 moles and the homopolymers from propylene oxide coordinated with only 1.6 moles.

Water of hydration is responsible for water solubility, and its presence explains why propylene oxide polymers are of limited water solubility but ethylene oxide/propylene oxide copolymers have extensive water solubility.

All ethylene oxide polymers are believed to be heliform in water, with hydration inside the helix.

At elevated temperatures, the helix is believed to elongate, upsetting the hydration and leading to insolubility.

The hydration of the ether linkages affects the solution viscosities.

Small amounts of water will actually raise the viscosity owing to an increase of the effective molecular weight.

This effect is decreased at elevated temperatures, the result of thermal energy breaking the water–ether association.

Solutions of Polyalkylene glycol at temperatures above their cloud point will separate into a water-rich layer and a layer rich in Polyalkylene glycol.

The thermal separation of Polyalkylene glycol from water can be a useful way of concentrating them from aqueous waste streams for disposal.

Because of the strong hydrogen bonding of water to Polyalkylene glycol, the freezing point of water in these polymers can be decreased.

This property is important in uses like brake fluids, where water crystals would cause the system to fail.

Solubilities:

The solubility of a Polyalkylene glycol is determined by its structure.

All Polyalkylene glycol is polar molecules and will dissolve in polar solvents.

The solubility of molecules derived from ethylene oxide will have water solubility and will be insoluble in nonpolar solvents.

The solubility of molecules derived from propylene oxide will be water insoluble, and will dissolve, at least to some level, in nonpolar solvents.

Molecules derived from butylene oxide or higher oxides will have increased oil solubilities and are manufactured to take advantage of this property.

Preparation of Capped Polyalkylene glycol

Polypropylene glycol dimethyl ether has become available as a commercial lubricant.

Although the conditions used commercially to effect this transformation are not reported, Polyalkylene glycol is almost certainly done by a Williamson ether synthesis.

The art of this transformation is the conversion of the alcohol into its alkoxide.

Sodium hydroxide is the most convenient base, and Polyalkylene glycol works well for low molecular weight ethoxylates.

Higher molecular weight ethoxylates can be capped by means of sodium hydroxide and a phase transfer catalyst.

Propoxylates, which are secondary alcohols, hence more difficult to convert to their alkoxide form, are normally capped by adding sodium or potassium methoxide and driving the equilibrium reaction between the different alkoxide forms to the polyether alkoxide by removing the methanol.

Capping efficiency is limited by the difficulty of converting all the end groups to the higher energy alkoxide species.

Improved yields can be obtained by using sodium hydride after the methoxide reaction has been driven as far as is practical or by using sodium hydride alone.

Synthesis of Polyalkylene glycol:

Ethylene oxide is a toxic material with a time-weighted average for 8 hours of exposure of 1 ppm and a short-term permissible limit of 5 ppm in a 15-minute period, as determined by the federal Office of Occupational Safety and Health (OSHA).

Polyalkylene glycol is highly flammable and has a wide flammable range in air of 3.0–100%.

Polyalkylene glycol can explosively decompose if exposed to an ignition source.

The flammability is only heightened by a boiling point of 10.48C, making Polyalkylene glycol a gas at ordinary temperatures.

Polyalkylene glycol can be polymerized with acidic, basic, and coordination catalysts, a polymerization that is very exothermic.

A very careful study of tile hazards and procedures for safely handling ethylene oxide must be undertaken before the use of this substance is attempted.

Similar hazards exists with propylene oxide and butylene oxide.

In the laboratory, Polyalkylene glycol is possible to use glass equipment at atmospheric pressure to prepare ethylene oxide, propylene oxide, and mixed ethylene oxide–propylene oxide polymers.

A nitrogen-flushed flask is charged with the starter solution and fitted with a dry-ice condenser.

A small amount of the epoxide is fed to the heated flask (typically 1008C or more) and allowed to reflux from the dry-ice condenser.

The epoxide charge will be slowly consumed by the polymerization reaction, and the reflux rate will decrease.

More epoxide is added at a rate sufficient to keep the system at reflux.

The rate can be increased by keeping the apparatus under a slight pressure from a dip tube immersed in an inert liquid.

The higher pressure increases the concentration of monomer in the reaction solution.

To make a random copolymer, the two oxides are co-fed; a block copolymer requires sequential feeds of the two different epoxides.

A similar system can be designed for coordinate-initiated polymerization.

The use of an autoclave for the polymerization will result in much faster rates, since operation at higher pressures is possible, resulting in much higher liquid phase concentrations of the monomers.

The epoxide can be fed either by forcing Polyalkylene glycol into the autoclave from a pressurized feed vessel with nitrogen pressure or by pumping Polyalkylene glycol into the reactor.

The reactor needs to be equipped with a cooling system and a control scheme to follow and regulate both pressure and temperature.

The reactor is heated to the desired operating temperature and the epoxide fed until the pressure has reached the desired level.

As the reaction progresses, the pressure will fall and more epoxide can be fed.

Pure ethylene oxide vapor can explosively decompose upon exposure to an ignition source.

A sufficient amount of nitrogen present before the initiation of the epoxide feed will ensure that the vapor phase does not reach the flammable limit at any time during the run.

Polyalkylene glycol is critical to keep the inventory of unreacted oxide in the reactor at a level such that the heat of polymerization (20 kcal/mol) can be removed by the cooling system.

A critical factor in keeping the oxide concentration low is the reactor temperature.

If pressure is the control mechanism, a low temperature in the reactor will allow the oxide to build to a potentially unsafe concentration.

Concentration of unreacted epoxides is the cause of the greatest number of reactor failures.

The problem becomes larger with propylene oxide and especially butylene oxide, where the vapor pressure of the oxide may not be a reliable indication of liquid phase concentration.

The reactor should have a safety relief device sized to handle a runaway reaction due to loss of cooling.

One of the authors has seen an autoclave and its high pressure cell catastrophically destroyed, with the autoclave top thrown many hundreds of feet.

The cause was the inadvertent feeding of ethylene oxide at a low temperature, an error that allowed the accumulation of a large inventory of ethylene oxide.

The uncontrolled polymerization that followed proved to be uncontainable.

To avoid exposure of personnel to unreacted ethylene oxide or propylene oxide, Polyalkylene glycol is necessary to hold the reactor contents at temperature after the end of the feed until the concentration of unreacted epoxides has dropped to an acceptable level.

This procedure is called a cook-out or digestion.

A cook-out may be necessary during synthesis because the vessel will fill with liquid as the reaction proceeds and the polymer is produced.

This will compress the nitrogen in the vessel, and the partial pressure of the monomer will therefore decrease (the system is run by keeping pressure constant).

The reaction rates will fall to unacceptably low levels.

Venting of the excess nitrogen after a cook-out will allow feed to be resumed at faster rates.

Polyalkylene glycol may even be necessary to remove some of the reactor’s liquid contents to allow room for further reaction.

This is most likely to occur during the synthesis of higher molecular weight products.

The commercial preparation of poly(alkylene oxides) is carried out in a manner analogous to that described for the laboratory autoclave.

A semibatch stainless steel system with a recirculation loop and an agitator has been described.

The reactions are carried out at 100–1208C at pressures of 60 psig.

The oxide feed rate is controlled by pressure, and feed times are on the order of 15 hours or more.

Pressindustria Company has reported a novel method for synthesizing Polyalkylene glycol.

The solution of growing polymer is sprayed through the headspace of a horizontal reactor.

The reaction with oxide monomer is reported to take place at the gas–liquid interface.

Rapid reactions without large increases in pressure or temperature are reported.

Cooling takes place with an external heat exchanger.

The first commercial-scale syntheses were performed at the Union Carbide production facility in Charleston, West Virginia.

The first preparations were similar to that used today.

Sodium salts of alcohols were used as starters at reaction temperatures slightly above those used currently.

Butanol was the starter alcohol of choice for monoethers.

The products developed at this time form the backbone of the UCON Fluids product line of Union Carbide and has been widely duplicated by other manufacturers.

The method first used at Union Carbide to neutralize these fluids was unusual.

The crude fluids were diluted with water, acidified with carbon dioxide, extracted with hot water, and then stripped of water at high temperature.

Decolorizing with activated charcoal was the last step.

Mechanism of Polymerization of Polyalkylene glycol:

Polyalkylene glycol is prepared by polymerizing epoxides with a starter that consists of an alcohol and a smaller amount of its metal alkoxide, usually the potassium or sodium salt.

The epoxide reacts with the metal alkoxide form of one of the starter alcohol molecules to give an alkoxide derivative of a new alcohol.

This new metal alkoxide is in equilibrium with all the alcohols present, so that the next reaction of an epoxide can occur either with the molecule that has already reacted or with a different alcohol.

The equilibrium between alcohol and alkoxide determines the molecular weight distribution of the product.

The epoxide monomers react with the metal salts of the alcohol at much faster rates than are observed with the alcohols.

Whichever alcohol is most acidic will tend to form the alkoxide salts and will be the most reactive toward the epoxide.

Once each starter alcohol has reacted with at least one epoxide, all molecules in the system will have approximately the same reactivity.

Unless the parent alcohol is extremely unreactive, the fast exchange of metal salt between the growing polymer chains then results in what is nearly a Poisson distribution for molecular weight.

The starter alcohols in commercial polymers use relatively reactive alcohols.

The Poisson distribution is a much narrower distribution than the most probable or Gaussian distribution.

In many applications the narrow distribution is critical, since Polyalkylene glycol means that there is no significant fraction of low molecular weight, volatile, or low-boiling components.

In addition, a narrow molecular weight distribution leads to a high viscosity index.

Ethylene oxide has two reactive sites, and the product is the same no matter which one reacts.

The situation is different with propylene oxide and butylene oxide.

In this case the ring opening occurs predominantly to produce a secondary hydroxyl group.

This result is due to steric factors; the methylene ring position is less hindered than the methylene.

For propylene oxide, 96% of the end groups are secondary hydroxyls and 4% are primary hydroxyls.

Copolymers of ethylene oxide and propylene oxide have two types of structure, random and blocked.

In the random polymer, the two epoxides are co-fed to the starter and will both be incorporated throughout the polymer.

They react to give a product that is itself reactive and is in the acid–base equilibrium with all the other alcohols and metal alkoxylates present.

To a first approximation, the epoxides are incorporated in a random manner dependent on the relative amounts of each epoxide present and the molecular weight distribution is still approximated by the Poisson model.

Polymers with this structure are identified as random copolymers.

In the block copolymer, an alternative structure is produced by reacting the starter first with one of the epoxides to produce a homopolymer.

This can then be reacted with a different epoxide to produce a block copolymer.

This name arises from the presence of a chain of one structure connected to a chain with a different structure.

The Polyalkylene glycol that are used commercially as lubricants are of five main types.

Homopolymers of propylene oxide (polypropylene glycols), which are the water-insoluble type.

These are typically monobutyl ethers.

Copolymers of ethylene oxide and propylene oxide, which are the water-soluble type.

These are typically diols or monobutyl ethers.

Polymers of butylene oxide.

These show greater oil solubility than the homopolymers of propylene oxide.

Polymers of propylene oxide and higher epoxides designed to give greater oil solubility.

Polymers of propylene oxide that are dimethyl ethers:

Polymers consisting of all ethyloxy groups, the polyethylene glycols, are not often used as lubricants, since they tend to crystallize at room temperature when their molecular weight exceeds 600.

Nevertheless, solid polyethylene glycols are used in specialty lubrication applications where the solid formulation is advantageous.

The tendency of polyethylene glycol chains to crystallize affects the block Polyalkylene glycol.

If the blocks of ethyloxy groups are long enough in a block copolymer, pastes or waxes result.

Block structures also tend to give the polymers surfactant properties in water.

As a result, block Polyalkylene glycol is often used as surfactants.

However, surfactant-like properties are of little use for most lubrication applications.

The epoxide polymers formed by base-catalyzed reactions typically have molecular weights of less than 20,000.

Traces of water in the monomer feed and minor side reactions limit the average molecular weight that can be achieved.

The major side reaction for the base-catalyzed polymerization of propylene oxide is the rearrangement of propylene oxide to allyl alcohol.

This was recognized as early as 1956.

The rearrangement involves deprotonation of the methyl group on the propylene oxide, followed by intramolecular ring opening.

This mechanism is supported by kinetic studies with 1, 2 epoxypropane-3,3,3-D, which show a large positive isotope effect.

The allyl alcohol formed reacts with ethylene oxide and propylene oxide to yield new Polyalkylene glycol molecules, which are monoallyl ethers.

This chain transfer reaction limits the ultimate molecular weight that can be achieved with base catalysis.

Although rearrangement of butylene oxide is not reported, this compound undoubtedly undergoes a similar base-catalyzed rearrangement.

Strong base catalysts that give reduced amounts of unsaturation are reported to be barium and strontium hydroxides.

An alternative technology for polymerization can produce much higher molecular weight ethylene oxide polymers.

Using coordinate-initiated polymerization, Polyalkylene glycol is possible to produce ethylene oxide polymers with molecular weights in excess of a million.

A calcium amide alkoxide suspended in a solvent that does not dissolve the polymer product is used.

Ethylene oxide is added and the polymer, not being soluble in the medium, is produced as a granular solid.

Polymerization is thought to take place by coordination of the epoxide to an electrophilic site on the catalysts.

This coordination activates the epoxide for reaction with the growing chain.

Nomenclature of Polyalkylene glycol:

Polyalkylene glycol is the common name for the homopolymers of ethylene oxide, propylene oxide, or butylene oxide; or the copolymers of ethylene oxide, propylene oxide, and/or butylene oxide.

Although Polyalkylene glycol is the common usage, Chemical Abstracts refers to these materials as polyoxyalkylene glycols.

The ethylene oxide polymers are generally called poly (ethylene glycols) or poly (ethylene oxides).

The Chemical Abstracts nomenclature is oxirane polymer.

The propylene oxide polymers are known as poly (propylene glycols) or poly (propylene oxides) with a Chemical Abstracts name of oxirane, methyl polymer.

The butylene oxide polymers are known as poly (butylene oxides) with a Chemical Abstracts name of oxirane, ethyl polymer.

The copolymers are known as “oxirane, polymer with methyloxirane” or “oxirane, methyl polymer with oxirane,” depending on which oxide was used in the greater amount.

Butylene oxide polymers are treated similarly.

The Chemical Abstracts nomenclature does not distinguish between random and blocked copolymers (see below).

The individual polymers and the copolymers all fall into the class of Polyalkylene glycol.

This latter name leads to the acronym Polyalkylene glycol.

The acronym PAO has occasionally been used to indicate poly (alkylene oxide), but PAO is commonly used to designate poly (a-olefin).

Mechanism of Polymerization Polyalkylene glycol is prepared by polymerizing epoxides with a starter that consists of an alcohol and a smaller amount of its metal alkoxide, usually the potassium or sodium salt.