SYNONYMS: PEI; POLYETHYLENEIMINE; polyethyleneimine; Polyethyleneimine; polyethylenemne; polyethylenemn; polyethylene; imin; imine; mn; mne; polietyhleneimin; poliethylenemne; poliethyleneimin; poliethyleneimine; polietilenimin; polietilenimine; polietilenmn; polietylenimine; polietylenmne; polietylenimin; Polyethyleneimine, branched, M.W. 600, 99%; Polyethyleneimine, branched, M.W. 1,800, 99%; Polyethyleneimine, branched, M.W. 70,000, 30% w/v aq. soln.; Polyethyleneimine, branched, M.W. 50,000 – 100,000, 30% w/w aq. soln.; Polyethylenimine, Branched, Mw 750,000, 33% w/v aq. soln. (bPEI 750000 33% soln.); polyethyleneimine, branched, M.W. 1,200, 99%; PEI-7;PEI-10;PEI-15;PEI-30;PEI-35;PEI-45;PEI-250;PEI-275;PEI-700;PEI-14M; Poly(ethyleneimine) solution ~50% in H; Polyethyleneimine, branched, M.W. 10,000, 99%; Poly(ethyleneimine) solution analytical standard, 50% (w/v) in H; Ethanolamine; Polyethylenimine; 2-AMINOETHYL HYDROGEN SULFATE; Ethyleneimine; POLYETHYLENEIMINE, BRANCHED;Aziridine,homopolymer;Ethyleneimine,homopolymer;polyethylenimine(10,000); polyethylenimine(20,000);polyethylenimine(35,000);polyethylenimine(40,000);Ethylene imine polymer solution; EPOMIN; epomin; Polymin P; polimin P; poliethylene imine; poliethyleneimine; POLIETHYLENEIMINE; polietilen; POLETLENMN; POL ETLEN MN; POL ETLENMNE; polietilen imin; polietilenimine; politilennimin; polyethylenimine; POLYETHYLENEIMINE; POLYETHYLENEIMIN; POLETLEN MN
Polyethyleneimine is clear viscous liquid.
Work described by Meyers and Royer¹ in 1977 has led to the commercial availability of a variety of products based upon polyethylenimine (PEI) technology. These include a variety of precious metal PEI catalysts* that are clearly advantageous over conventional supported and unsupported catalysts in areas such as benzyltype protectinggroup cleavage, reductions of aromatic-nitro groups and peptide syntheses.
COMPOSITION
The monomer is easy to describe. It consists of a three-membered ring. Two corners of the molecule consist of -CH2- linkages. The third corner is a secondary amine group, =NH. In the presence of a catalyst this monomer is converted into a highly branched polymer with about 25% primary amine groups, 50% secondary amine groups, and 25% tertiary amine groups. This product is sometimes called “pure polyethyleneimine” in order to differentiate it from certain copolymers of ethyleneimine and acrylamide. The latter mixture is copolymerized to produce so-called “modified PEI,” that has a molecular mass up to about 2 million grams per mole. Each of these types of products is delivered to the mill in the form of viscous solutions. Solids contents are the range of about 10 to 50%, depending on molecular mass.
Melting point:59-60°C
Boiling point:250 °C(lit.)
Density 1.030 g/mL at 25 °C
refractive index n20/D 1.5290
Flash point:>230 °F
storage temp. 2-8°C
form Liquid
color Pale yellow
Water Solubility Soluble in water.
Sensitive Hygroscopic
SOLUBILITY
Liquid Solubility Soluble in toluene, methanol, ethanol, chloroform and xylene. Insoluble in water, alcohol, benzene, ethyl ether and acetone.
FUNCTION
Pure PEI is very effective for neutralization of excess anionic colloidal charge, especially under acidic and neutral pH conditions. Modified PEI copolymers having relatively high molecular mass can be effective for drainage and pitch control.
Branched Polyethylenimine, Mw 2,000,000, 25% w/v aq. soln. (bPEI 2000000 25% soln.) is highly branched polyamine with high cationic charge density. bPEI 2000000 contains primary, secondary, and tertiary amine groups with pH 8.
Industrially, branched polyethylenimine (bPEI) have extensive applications as an auxiliary agent intensifying manufacturing processes and improving quality of the final products. Branched Polyethylenimine are widely used in: paper-making, water treatment, detergents, adhesives, and cosmetics. In research, Branched Polyethylenimine are extensively investigated as non-viral vector carriers.
Crosslinked derivatives of PEI are potential chromatographic supports and ion exchangers because of their binding capacity for a wide range of metals. Applications would likely include purification of mercurycontaminated waste water and precious-metal reclamation.
PEI immobilized on a rigid inorganic matrix of high porosity is ideal for use in columns or in suspension (without magnetic stirrers). It binds polyanions, such as nucleic acids, very strongly. Suggested applications include chromatography of proteins, nucleotides and nucleic acids. It also effectively binds metal ions such as Ni2+, Pd2+, Pt2+, Co2+ and Cu2+.
Supported on an inorganic powder, this resin is suitable for use in suspension with magnetic stirrers and is usually conducive to rapid removal by filtration or centrifugation.
The PEI powder has been used in the chromatographic resolution of adenosine, AMP, ADP and ATP with a sodium chloride gradient. All components were recovered in 100% yield, unchanged, as shown by TLC and highvoltage electrophoresis.
These resins show a greater degree of hydrophobic character because of pendant benzyl groups, and strongly bind anions with polar components.
ADVANTAGES
The highest cation density among other existing materials.
Very high reactivity.
Water solubility.
STRAGETIES FOR USE
The branched nature and exceptionally high charge of pure PEI make it an excellent choice for treatment of highly anionic furnish, furnish that has a high electrical conductivity, or thick-stock furnish. The branched structure is believed to provide some resistance to penetration of the molecule into very small slit-like pores in the fiber cell wall. The colloidal charge, filtrate turbidity, and drainage characteristics of the furnish should be monitored when selecting or optimizing PEI dosage. The modified PEI copolymer is usually added relatively late in the thin-stock cycle in order to achieve a significant boost in first-pass retention and the rate of drainage. Neither additive is expected to be cost-effective in furnish having pH values in excess of about 8, since the amine groups rapidly lose their charged character above that point. Likewise, strongly varying pH values are expected to cause variations in the performance of PEI products.
APPLICATIONS
Polyethyleneimine, branched, M.W. 10,000 acts as an auxiliary agent. It is used in paper-making, water treatment, detergents, adhesives and cosmetics. It is investigated as non-viral vector carriers in research.
Anchor coating agents, Flocculants, Cation agent, Adhesive modifier
Used as a polyelectrolyte multilayer on charged surfaces to provide a biocompatible coating on surfaces.Detergents, adhesives, water treatment, printing inks, dyes, cosmetics, and paper industry, adhesion promoter, lamination primer, fixative agent, flocculant, cationic dispersant, stability enhancer, surface activator, chelating agent, scavenger for aldehydes and oxides.
Polietilenimin, berrak viskoz svdr.
Meyers ve Royer tarafndan 1977’de tanmlanan i, polietilenimin (PEI) teknolojisine dayanan çeitli ürünlerin ticari olarak bulunmasna neden olmutur. Bunlar, benzil-tipi koruma grubu yarlmas, aromatik-nitro gruplarnn indirgenmesi ve peptid sentezleri gibi alanlarda geleneksel olarak desteklenmi ve desteklenmeyen katalizörlere kyasla açkça avantajl çeitli deerli metal PEI katalizörleri * içerir.
BLETRME, KOMPOZSYON
Monomerin tanmlanmas kolaydr. Üçlü bir halkadan oluur. Molekülün iki köesi -CH2- balarndan oluur. Üçüncü köe, ikincil bir amin grubu, = NH’dir. Bir katalizörün mevcudiyetinde bu monomer, yaklak% 25 birincil amin gruplar,% 50 ikincil amin gruplar ve% 25 üçüncül amin gruplar ile çok dallanm bir polimer haline dönütürülür. Bu ürün bazen etilenimin ve akrilamidin baz kopolimerleri arasndan ayrt etmek için bazen “saf polietilenimin” olarak adlandrlr. Son karm, mol bana yaklak 2 milyon gram molekül kütlesine sahip olan “modifiye PEI” üretmek üzere kopolimerletirilir. Bu tür ürünlerin her biri viskoz çözeltiler eklinde deirmene teslim edilir. Kat maddeler moleküler kütleye bal olarak yaklak% 10 ila 50 aralndadr.
Erime noktas: 59-60 ° C
Kaynama noktas: 250 ° C (aydnlk)
Younluk 1.030 g / mL, 25 ° C’de
krlma indisi n20 / D 1.5290
Parlama noktas:> 230 ° F
saklama derecesi. 2-8 ° C
Sv Form
soluk sar
Suda Çözünürlük Suda özünebilir.
Hassas Higroskopik
ÇÖZÜNÜRLÜK
Sv Çözünürlüü Tolüen, metanol, etanol, kloroform ve ksilen içinde çözülür. Su, alkol, benzen, etil eter ve asetonda çözünmez.
LEV
Saf PEI, özellikle asidik ve nötr pH koullarnda ar anyonik koloidal yükün nötrletirilmesi için çok etkilidir. Nispeten yüksek moleküler kütleye sahip deitirilmi PEI kopolimeri, drenaj ve zift kontrolü için etkili olabilir.
Dallanm Polietilenimin, Mw 2,000,000, arlk / arlk% 25 aq. çöz. (bPEI 2000000% 25 solüsyon) yüksek katyonik yük younluuna sahip yüksek oranda dall poliamindir. bPEI 2000000, pH 8 olan birincil, ikincil ve üçüncül amin gruplarn içerir.
Endüstride dall polietilenimin (bPEI), imalat süreçlerini younlatran ve nihai ürünlerin kalitesini arttran yardmc bir ajan olarak geni uygulamalara sahiptir. Dallanm Polietilenimin, kat yapm, su artm, deterjanlar, yaptrclar ve kozmetik alanlarnda yaygn olarak kullanlmaktadr. Aratrmada, Dall Polietilenimin, yaygn olarak viral olmayan vektör tayclar olarak aratrlmtr.
PEI’nin çapraz bal türevleri, geni bir metal aral için balanma kapasiteleri nedeniyle potansiyel kromatografik destekler ve iyon deitiricilerdir. Bavurular büyük olaslkla cva kirli kontamine atk suyun artlmas ve kymetli madenlerin slah içerecektir.
Yüksek gözeneklilie sahip kat bir inorganik matriste hareketsizletirilmi olan PEI, kolonlarda veya süspansiyonda (manyetik kartrclar olmadan) kullanm için idealdir. Nükleik asitler gibi polianyonlar çok güçlü bir ekilde balar. Önerilen uygulamalar protein, nükleotid ve nükleik asitlerin kromatografisini içerir. Ayn zamanda Ni2 +, Pd2 +, Pt2 +, Co2 + ve Cu2 + gibi metal iyonlarn etkili bir ekilde balar.
norganik bir toz üzerinde desteklenen bu reçine, manyetik kartrclarla süspansiyon halinde kullanma uygundur ve genellikle filtrasyon veya santrifüjle hzl bir ekilde uzaklatrlmaya elverilidir.
PEI tozu, adenosin, AMP, ADP ve ATP’nin bir sodyum klorür gradyan ile kromatografik çözünürlüünde kullanlmtr. Tüm bileenler, TLC ve yüksek voltaj elektroforeziyle gösterildii gibi, deimeden% 100 verimle elde edildi.
Bu reçineler sarkk benzil gruplar nedeniyle daha fazla hidrofobik karakter gösterirler ve anyonlar kutupsal bileenlerle kuvvetle balarlar.
AVANTAJLARI
Mevcut dier malzemeler arasnda en yüksek katyon younluu.
Çok yüksek reaktivite.
Su çözünürlüü.
KULLANIM STRATEJLER
Dallanm tabiat ve saf PEI son derece yüksek arj, yüksek bir elektrik iletkenliine sahip yüksek oranda anyonik bir döeme, veya kaln stoklu mobilyann tedavisi için mükemmel bir seçimdir. Dall yapnn, molekülün lif hücresi duvarndaki çok küçük yark benzeri deliklere nüfuz etmesine bir miktar direnç salad düünülmektedir. PEI dozajn seçerken veya optimize ederken, ambalajn koloidal yükü, filtrat bulankl ve drenaj özellikleri izlenmelidir. Modifiye edilmi PEI kopolimeri, ilk geçi tutma oranndaki ve drenaj oranndaki belirgin art salamak için genellikle ince stok çevriminde nispeten geç eklenir. Ne katk maddesinin, yaklak 8’den fazla pH deerine sahip olmas, bu amin gruplarnn hzla yüklü karakterini bu noktadan daha fazla kaybetmesinden dolay, maliyet açsndan etkili olmas beklenir. Ayn ekilde, kuvvetle deien pH deerlerinden PEI ürünlerinin performansnda deiikliklere neden olmas beklenir.
UYGULAMALAR
Polietilenimin, dallanm, M.W. 10,000, bir yardmc madde olarak ilev görür. Kat yapmnda, su artmnda, deterjanlarda, yapkanlarda ve kozmetiklerde kullanlr. Aratrmalarda viral olmayan vektör tayclar olarak aratrlmtr.
Çapa kaplama maddeleri, Phtlama önleyiciler, Katyon ajan, Yaptrc deitirici
Yüzeylerde biyolojik olarak uyumlu bir kaplama salamak için yüklü yüzeylerde polielektrolit çok tabakal olarak kullanlr. Deterjanlar, yapkanlar, su artm, bask mürekkepleri, boyalar, kozmetik ve kat endüstrisi, yapma arttrc, laminasyon astar, fiksatif madde, phlatrc, katyonik dispersan, stabilite arttrc , yüzey aktifletirici, kenetleme maddesi, aldehitler ve oksitler için süpürücü.