PVA 2488 (POLYVINYL ALCOHOL 2488) (POLVNL ALKOL 2488)

PVA 2488 (POLYVINYL ALCOHOL 2488) (POLVNL ALKOL 2488)

PVA 2488 (POLYVINYL ALCOHOL 2488) (POLVNL ALKOL 2488)

CAS No: 9002-89-5

Synonyms: Ethenol; VINYL ALCOHOL; POLYVINYL ALCOHOL; 9002-89-5; Hydroxyethene; Hydroxyethylene; Ethenol, homopolymer; Gohsenol; Polyviol; Elvanol; Mowiol; Poval; Poly(vinyl alcohol); vinylalcohol; 557-75-5; Alcotex 17F-H; Alkotex; Gelvatol; Rhodoviol; EINECS 209-183-3; Polydesis; Polyvinol; Vinalak; Vinarol; Vinarole; Alvyl; Covol; Lemol; Gohsenol GH; Lamephil OJ; Sloviol R; Kuralon VP; Vinacol MH; Vinarol DT; Vinarol ST; Aracet APV; Enbra OV; Gtohsenol GL 05; Polysizer 173; Cipoviol W 72; Gohsenol AH 22; Gohsenol GH 17; Vinavilol 2-98; Elvanol T 25; Gosenol KH-17; Sumitex H 10; Gelvatol 1-30; Gelvatol 1-60; Kurare Poval 120; Kurare 217; Rhodoviol 4/125; Lemol GF-60; Poval 205S; Alcotex 88/05; Alcotex 88/10; ;Alcotex 99/10; Poval 120; Poval 203; Vinyl alcohol, polymers; Polyviol MO 5/140; Mowiol N 30-88; GLO 5; PVS 4; Poly(vinyl alcohol), 98% hydrolyzed, approx. M.W. 13,000; polyvinylalcohol; Vinol; Poly(vinyl alcohol), 88% hydrolyzed, average M.W. 20000-30000; Poly(vinyl alcohol), 99-100% hydrolyzed, approx. M.W. 124,000; Poly(vinyl alcohol), 88% hydrolyzed, average M.W. 145,000-180,000; Poly(vinyl alcohol), 88% hydrolyzed, average M.W. 85,000-120,000; Poly(vinyl alcohol), 87.0-89.0% hydrolyzed, M.W. approx. 13,000-23,000; Poly(vinyl alcohol), 87.0-89.0% hydrolyzed, M.W. approx. 31,000-50,000; Poly(vinyl alcohol), 92.0-94.0% hydrolyzed,M.W. approx. 146,000-186,000; Poly(vinyl alcohol), 95.5-96.5% hydrolyzed, M.W. approx. 85,000-124,000; Poly(vinyl alcohol), 98.0%-98.8% hydrolyzed, M.W. approx. 50,000-85,000; Poly(vinyl alcohol), 98.0-98.8% hydrolyzed, M.W. approx. 31,000-50,000; Poly(vinyl alcohol), 98.0-98.8% hydrolyzed,M.W. approx. 146,000-186,000; PVA 008; GH 20; GL 02; PVAL 45/02; PVAL 55/12; Gohsenol NL05; Warcopolymer A 20; EP 160; Vinyl alcohol polymer; FH 1500; Vinylon Film 2000; Vinylon Film 3000; Vinol 125; Vinol 205; Vinol 351; Vinol 523; CH2=CHOH; Polyvinyl alcohol 17-99; Polyvinylacetate, hydrolyzed; M 13/20; Vinylon Film VF-A 2500; PVA 17-99; VPB 105-2; AKOS006229012; Poly(vinyl alcohol) (Fully hydrolyzed-very Low M.Wt.) MW 7.000-10.000; vinil alkol; vinyl alcol; polivinil alkol; poli vinil alkol 24/88; poliviyol; PVA 24/88; PVA 2 4 8 8; PVA 24-88; poli(vinil alkol); hidroksi etilen; hidroksietilen; etenol; eten-ol; hidroksi eten; hidroksieten; etenol homopolimer; polivol; gosenol; polivinol; polivin ol; polivin-ol; polivinil alcol; Acetic Acid Ethenyl Ester co-Polymer with Ethenol; PVAI; PVOH; Poly(Ethenol), Ethenol, homopolymer; PVA; Polyviol; Vinol; Alvyl; Alcotex; Covol; Gelvatol; Lemol; Mowiol; Mowiflex, Alcotex, Elvanol, Gelvatol, Lemol, Mowiol, Nelfilcon A, Polyviol und Rhodoviol; Alcool polyvinylique; POLYVINYL ALCOHOL, BUTYRALDEHYDE ACETAL, SULFONATE, SODIUM SALT; Alcool de polyvinyle; Alcool polyvinylique;
CAS:9002-89-5
MF:C2H4O
MW:44.05256
EINECS:209-183-3
Melting point:>300 °C
Boiling point:-14.5°C (rough estimate)
Density 1.30
refractive index 1.3810 (estimate)
Flash point:79°C
storage temp. Store below +30°C.
solubility H2O: soluble (hot)
form Powder
color White to cream
PH3.5-7.0 (40g/l, H2O, 20℃)
Water Solubility soluble in hot water
Merck 14,7585
Stability:Stable. Combustible. Dust may form explosive mixtures with air. Incompatible with strong oxidizing agents.
Polyvinyl Alcohol, Reagent, also known as PVA or PVAI, is a synthetic polymer used in textiles, papermaking, and several types of coatings. The Reagent grade denotes that this chemical is the highest quality commercially available and that the American Chemical Society has not officially set any specifications for this material. Spectrum Chemical manufactured Reagent grade products meet the toughest regulatory standards for quality and purity.
Poly(vinyl alcohol) (PVOH, PVA, or PVAl) is a water-soluble synthetic polymer. It has the idealized formula [CH2CH(OH)]n. It is used in papermaking, textile warp sizing, as a thickener and emulsion stabilizer in PVAc adhesive formulations and a variety of coatings. It is colourless (white) and odorless. It is commonly supplied as beads or as solutions in water.
Uses
PVA is used in a variety of medical applications because of its biocompatibility, low tendency for protein adhesion, and low toxicity. Specific uses include cartilage replacements, contact lenses, and eye drops.[5] Polyvinyl alcohol is used as an aid in suspension polymerizations. Its largest application in China is its use as a protective colloid to make polyvinyl acetate dispersions. In Japan its major use is the production of Vinylon fiber.[6] This fiber is also manufactured in North Korea for self-sufficiency reasons, because no oil is required to produce it. Another application is photographic film.[7]

Medically, it may also used as the embolic agent in a Uterine Fibroid Embolectomy (UFE) [8]

Polyvinyl acetals
Polyvinyl acetals are prepared by treating PVA with aldehydes. Butyraldehyde and formaldehyde afford polyvinyl butyral (PVB) and polyvinyl formal (PVF), respectively. Preparation of polyvinyl butyral is the largest use for polyvinyl alcohol in the U.S. and Western Europe.

 

Preparation
Unlike most vinyl polymers, PVA is not prepared by polymerization of the corresponding monomer as the monomer, vinyl alcohol, is thermodynamically unstable with respect to its tautomer acetaldehyde. Instead, PVA is prepared by hydrolysis of polyvinyl acetate[3], or sometimes other vinyl ester-derived polymers with formate or chloroacetate groups instead of acetate. The conversion of the polyvinyl esters is usually conducted by base-catalysed transesterification with ethanol:

[CH2CH(OAc)]n + C2H5OH → [CH2CH(OH)]n + C2H5OAc
The properties of the polymer are affected by the degree of transesterification.

Worldwide consumption of polyvinyl alcohol was over one million metric tons in 2006.[6] Large producers include Kuraray (Japan, Europe, and US) and Sekisui Specialty Chemicals (US), while mainland China has installed a number of very large production facilities in the past decade and currently accounts for 45% of world capacity.

Structure and properties
PVA is an atactic material that exhibits crystallinity. In terms of microstructure, it is composed mainly of 1,3-diol linkages [-CH2-CH(OH)-CH2-CH(OH)-] but a few percent of 1,2-diols [-CH2-CH(OH)-CH(OH)-CH2-] occur, depending on the conditions for the polymerization of the vinyl ester precursor.[3]

Polyvinyl alcohol has excellent film forming, emulsifying and adhesive properties. It is also resistant to oil, grease and solvents. It has high tensile strength and flexibility, as well as high oxygen and aroma barrier properties. However, these properties are dependent on humidity: water absorbed at higher humidity levels acts as a plasticiser, which reduces the polymer’s tensile strength, but increases its elongation and tear strength.

Safety and environmental considerations
PVA is widely used, thus its toxicity and biodegradation are of interest. Solutions containing up to 5% PVA are nontoxic to fish.[3] It biodegrades slowly.
Chemical formula (C2H4O)x
Density 1.19-1.31 g/cm3
Melting point 200 °C (392 °F; 473 K)
log P 0.26 [1]
Refractive index (nD) 1.477 @ 632 nm
Flash point 79.44 °C (174.99 °F; 352.59 K)
Lethal dose or concentration (LD, LC):
LD50 (median dose) 14,700 mg/kg (Mouse)
Except where otherwise noted, data are given for materials in their standard state (at 25 °C [77 °F], 100 kPa).
Cold soluble Polyvinyl Alcohol(PVA-2488), organic chemical compound, white flake-shape, flocculent or powder solid, odorless. It can be quickly and fully dissolved in tap water and cold water. However, it can’t be dissolved in gasoline, kerosene, vegetable oil, benzene, toluene, dichloroethane, carbon tetrachloride, acetone, vinyl acetate, methanol, glycol and so on. It can be slightly dissolved in dimethyl sulphoxide. PVA is important chemical raw material.

 

2. Product Specifications Parameter:

Item

PVA

Average Polymerization（ DP）

1700-1800

　Molecular Weight（ Mn）

84000-89000

　Viscosity（cps）

21-26

　Alkalization（ mole%）

86-89

　Volatile（ wt%）

＜ 5

　Ash（ wt%）

＜ 0.5

　PH Value

5-7

　Fineness（mesh）

＞ 120
Polyvinyl alcohol is high polymer with excellent characters to dissolve easily in water but not to dissolve in common organic solvent and organic acids, and with excellent film-forming property,oil resistant, chemical-resistant. It can react with formaldehydes to form polyvinyl acetal.
The PVA production facilities of our company have been perfecting day by day with the long-term absorption and technological transformation on the basis of importing the complete set of technology from European Company. PVA produced by our company is good in performances and stable in quality. It enjoys a great reputation both at home and abroad.
3. Product Applications:

This product is mainly used in internal & external putty, interface agent, ceramic adhesive, gypsum plaster, which can increase the cement, mortar’s adhesive, flowing performance effectively, also can slow down cement surface drying time, increasing painting adaptability and prevent the crack of cement coating.

 

4. Product Package and Usage:

25kg Paper Bag. Stored under normal temperature, pay attention not to get wet.

Every 1 ton mortar, 8-10kg usage of this product recommended.
PVA 2488 by Liwei chemical (Sinochem) is fully hydrolyzed, polyvinyl alcohol high polymer grade. Soluble in water while insoluble in organic solvent and organic acids. Exhibits excellent film-forming property, oil resistance, chemical resistance and good stability. It can react with formaldehydes to form polyvinyl acetal. PVA 2488 by Liwei chemical (Sinochem) is recommended for raw materials of vinylon fibers, construction, paint additives, mainly used in textile and fabric finishing agents.
Polyvinyl alcohol (PVA) resin is a high molecular polymer with a chemical formula of (CH2CHOH)n. It is a commonly used adhesive with good film forming properties, bonding properties and thermal stability. Its water solubility is related to the degree of alcoholysis. When the degree of alcoholysis is below 88%, polyvinyl alcohol can be dissolved in normal temperature water; when the degree of alcoholysis reaches 97%, hot water of 60-80 degrees C should be required for dissolution.

Specification Hydrolysis
(mol%)

Viscosity
(cps)

Volatiles
（%）

Ash content（%） PH
1788 86.0-89.0 20.0-26.0 Max 7.0 Max 7.0 5-7
2488 86.0-89.0 44.0-52.0 Max 7.0 Max 7.0 5-7
Physical properties

Appearance: white free-flowing powder, odorless and tasteless.
Solubility: Polyvinyl alcohol powder (PVA) 17-88 and 24-88 type are partially alcoholy-soluble types which can be soluble in room temperature water. It is prohibited to use when the temperature drops to below 0 degree C; when the temperature is below 10 degrees C, sufficient dissolution time is required for dissolution, usually takes 5-10 minutes.
Solution stability: Aqueous solution of low viscosity Polyvinyl alcohol is stable at room temperature and does not deteriorate during storage.
Film Formability: Due to the high adhesion strength between Polyvinyl alcohol molecules, Polyvinyl alcohol is easy to form a film, which has colorless and transparent smooth surface with high mechanical strength and good solvent resistance.

Application field
1, Polyvinyl alcohol can be applied in a variety of wall putty, drymix mortar, gypsum products, tile adhesive. It can effectively increase the adhesion of cement, ash calcium powder and gypsum. It can increase fluidity and slow the surface drying time to prevent product surface from cracking. It is suitable for wall/ceiling finishes and tile pastes.
2, adding 1-2KG of Polyvinyl alcohol with fineness above 300 meshes, into the latex paint production process, can effectively improve the smoothness of the product, improve the film formation and reduce the amount of emulsion used 5-10KG.
3, in the thermal insulation mortar system, 1 KG of Polyvinyl alcohol (160 mesh) has the similar effect of 4-5KG latex powder. In practical application, combine latex powder and Polyvinyl alcohol to use will achieve a better effect.
E Anlamllar: Ethenol; VINYL ALCOHOL; POLYVINYL ALCOHOL; 9002-89-5; Hydroxyethene; Hydroxyethylene; Ethenol, homopolymer; Gohsenol; Polyviol; Elvanol; Mowiol; Poval; Poly(vinyl alcohol); vinylalcohol; 557-75-5; Alcotex 17F-H; Alkotex; Gelvatol; Rhodoviol; EINECS 209-183-3; Polydesis; Polyvinol; Vinalak; Vinarol; Vinarole; Alvyl; Covol; Lemol; Gohsenol GH; Lamephil OJ; Sloviol R; Kuralon VP; Vinacol MH; Vinarol DT; Vinarol ST; Aracet APV; Enbra OV; Gtohsenol GL 05; Polysizer 173; Cipoviol W 72; Gohsenol AH 22; Gohsenol GH 17; Vinavilol 2-98; Elvanol T 25; Gosenol KH-17; Sumitex H 10; Gelvatol 1-30; Gelvatol 1-60; Kurare Poval 120; Kurare 217; Rhodoviol 4/125; Lemol GF-60; Poval 205S; Alcotex 88/05; Alcotex 88/10; ;Alcotex 99/10; Poval 120; Poval 203; Vinyl alcohol, polymers; Polyviol MO 5/140; Mowiol N 30-88; GLO 5; PVS 4; Poly(vinyl alcohol), 98% hydrolyzed, approx. M.W. 13,000; polyvinylalcohol; Vinol; Poly(vinyl alcohol), 88% hydrolyzed, average M.W. 20000-30000; Poly(vinyl alcohol), 99-100% hydrolyzed, approx. M.W. 124,000; Poly(vinyl alcohol), 88% hydrolyzed, average M.W. 145,000-180,000; Poly(vinyl alcohol), 88% hydrolyzed, average M.W. 85,000-120,000; Poly(vinyl alcohol), 87.0-89.0% hydrolyzed, M.W. approx. 13,000-23,000; Poly(vinyl alcohol), 87.0-89.0% hydrolyzed, M.W. approx. 31,000-50,000; Poly(vinyl alcohol), 92.0-94.0% hydrolyzed,M.W. approx. 146,000-186,000; Poly(vinyl alcohol), 95.5-96.5% hydrolyzed, M.W. approx. 85,000-124,000; Poly(vinyl alcohol), 98.0%-98.8% hydrolyzed, M.W. approx. 50,000-85,000; Poly(vinyl alcohol), 98.0-98.8% hydrolyzed, M.W. approx. 31,000-50,000; Poly(vinyl alcohol), 98.0-98.8% hydrolyzed,M.W. approx. 146,000-186,000; PVA 008; GH 20; GL 02; PVAL 45/02; PVAL 55/12; Gohsenol NL05; Warcopolymer A 20; EP 160; Vinyl alcohol polymer; FH 1500; Vinylon Film 2000; Vinylon Film 3000; Vinol 125; Vinol 205; Vinol 351; Vinol 523; CH2=CHOH; Polyvinyl alcohol 17-99; Polyvinylacetate, hydrolyzed; M 13/20; Vinylon Film VF-A 2500; PVA 17-99; VPB 105-2; AKOS006229012; Poly(vinyl alcohol) (Fully hydrolyzed-very Low M.Wt.) MW 7.000-10.000; vinil alkol; vinyl alcol; polivinil alkol; poli vinil alkol 24/88; poliviyol; PVA 24/88; PVA 2 4 8 8; PVA 24-88; poli(vinil alkol); hidroksi etilen; hidroksietilen; etenol; eten-ol; hidroksi eten; hidroksieten; etenol homopolimer; polivol; gosenol; polivinol; polivin ol; polivin-ol; polivinil alcol; Acetic Acid Ethenyl Ester co-Polymer with Ethenol; PVAI; PVOH; Poly(Ethenol), Ethenol, homopolymer; PVA; Polyviol; Vinol; Alvyl; Alcotex; Covol; Gelvatol; Lemol; Mowiol; Mowiflex, Alcotex, Elvanol, Gelvatol, Lemol, Mowiol, Nelfilcon A, Polyviol und Rhodoviol; Alcool polyvinylique; POLYVINYL ALCOHOL, BUTYRALDEHYDE ACETAL, SULFONATE, SODIUM SALT; Alcool de polyvinyle; Alcool polyvinylique;
Polivinil alkol (PVA) reçine bir tür ar polimerdir. Genellikle beyaz veya hafif sar bir floküle, pul, granül veya toz halinde bir görünümdür.
PVA toksik olmayan, insipid ve kirletici deildir. PVA, iyi kimyasal kararlla sahip bir tür suda çözünür reçinedir. Ayrca iyi yapma, film oluturma yetenei, yaltm, ya direnci, anma direnci ve gaz bariyer özellikleri vardr ve poliollerin tipik kimyasal özelliklerine sahiptir ve esterifikasyon, eterletirme, asetizasyon reaksiyonlar yapabilir.
Ürün kullanr
1. Tekstil endüstrisinde, esas olarak iplik hamuru, kuma terbiye ajanlar ve vinylon elyaflarnn hammaddeleri olarak kullanlrlar;
2. Inaat ve dekorasyon sektörlerinde, harç çimento katk maddeleri, iç ve d duvarlar için boya katk maddeleri ve kalplama plaka yaptrclar olarak kullanlabilir;
3. Kimya endüstrisinde, PVF, asetal ve butiral reçineleri üretimi için polimerizasyon emülgatörleri, dispersanlar ve hammadde olarak kullanlabilir;
4. lumbering ve kat yapm endüstrisinde, yaptrclar olarak kullanlabilir;
5. Tarmda, toprak arttrc, pestisit yapma sinerjisti ve PVA filmi olarak kullanlabilir;
6. Petrol sömürüsünde, iyi çimentolama ajanlar olarak kullanlabilir.
7. Ayrca, kozmetik, ilaç, bask, seramik, çelik, elektronik, elektrokaplama ve benzeri alanlarda da kullanlabilirler.
Ambalaj
Ambalaj: küçük paket: 20/25kgs kat torbalar
Toplu paket: toplu çanta bana 600-700kgs
Depolama ve tama
Depolama: kapal iyi havalandrlm ve kuru bir odada saklanmaldr. Nem, güne ve yamur pozlama önlemek.
Ulam: nakliye srasnda, ambalaj torbalarnn zarar görmesini önlemek için ürünler hafifçe hareket ettirilmelidir. Bir atele yakalandklarnda, çplak alevle dorudan temastan kaçnn, yangn söndürmek için herhangi bir yangn söndürücüler kullann.
Polivinil asetatlardan, asetat gruplarnn hidroksil gruplar ile deitirilmesi ile hazrlanan bir polimerdir. Polivinil Alkol (PVA) vinil alkolün polimerizasyonuyla elde edilebilen suda çözünebilen sentetik polimerdir.
PVA doal bir kimyasal olarak ortaya çkt u zamana kadar tespit edilememitir.
Hem hidrofilik hem de hidrofobik fonksiyonel gruplara sahiptir. Bundan dolay baz üretim süreçlerinde yüzey aktif madde olarak kullanlmaktadr.
Bu hammaddenin snflar moleküler arlk ve hidroliz derecesi snflarn göre deiir. Moleküler arlk genellik çözelti viskozitesi açsndan ifade edilir.
Polivinil Alkol’ün yüzey aktif maddeler, slatclar, köpük gidericiler ve kvam arttrclar ile yaplan emülsiyonlar sonucunda mikroorganizmalara kar savunmasz hale gelmektedir.
Tutkal, reçine ,sünger üretimi ,kat veya tekstil sektöründe ara ajan olarak kullanlr.
PEI, nanofiber oluturma özelliini arttrmak için polivinil alkol (PVA) ile çözelti haline getirilerek kullanlmtr. Elektrospinleme ilemine uygun PEI/PVA oran %10 olarak belirlenerek hazrlanan PVA-PEI çözeltisinden, elektrospinleme yöntemiyle nanofiber yap üretilmitir. Ardndan PVA-PEI nanofiber yapsnn kullanm alan uygulamas yaplmtr. PVA-PEI nanofiber yapsna farkl nitelikler kazandrmak ve polimer esasl nanofiber yap çeitliliine katkda bulunmak için GO katks yaplmtr. Optimum PVA-PEI-GO oran 100:10:5 olacak ekilde belirlenerek hazrlanan PVA-PEI-GO çözeltisinden elektrospinleme yöntemiyle nanofiber üretimi gerçekletirilmitir. Üretilen PVA, PVA-PEI ve PVA-PEI-GO nanofiber yaplarnn termal karakterizasyonu termogravimetrik analiz (TGA) ve diferansiyel taramal kalorimetri (DSC) ile, yüzey karakterizasyonu taramal elektron mikroskobuyla (SEM), yapsal karakterizasyonu Fourier Transform Infrared (FT-IR) Spektrometresi analizleri ile yaplm ve birbirleriyle kyaslanmtr. v Çalmann sonunda, PVA’ya PEI katksyla birlikte nanofiberlerin yapsnda dallanmann, çapraz balanma younluunun ve çaplarn artt fakat termal kararlln azald görülmütür. PVA-PEI nanofiber yapsna GO katksnn ise dallanma ve çapraz balanma younluunun daha fazla arttrarak, nanofiber çaplarn küçülttüü ve termal kararll arttrd görülmütür.
Özellikleri: Polivinil alkol suda çözünür bir polimerdir. Bir polivinil esterinin (polivinil asetat) hidroliziyle hazrlanr.
Kullanm alanlar: Dier reçinelerin hazrl için bir balangç maddesi olarak kullanlr. Süngerlerin üretiminde kullanlan elastomerlerin bir komponenti olarak kullanlabilir. Bu polimer kat veya tekstiller üzerinde yalar ve makine yalarna dayankllk veren aharlama ajanlar olarak kullanlrlar, filmleri solventler veya oksijen tarafndan saldrya dayankl yapmak için kullanlr. Polivinil alkol ayrca yaptrclarn, emülsifiyerlerin, süspanse edici ve klnlatrc (kvam verici) ajanlarn bir komponenti olarak kullanlabilir. laç endüstrisinde, polivinil alkol optalmik yalayc ve viskosite artrc ajan olarak kullanlmaktadr. Polivinil alkol, gözlerdeki göz yann doal filmini kalnlatrr.
Provinil alkol suda çözünen bir etkendir.

Kat yapmnda Tekstil ve çeitli kaplamalarda kullanlr.
Beyaz renke sahiptir. Ve kokusu hiç yok denilebilecek kadar yoktur suda çözünebilir.
Provinil alkol (pva) ve sodyum aljinat ile karm elektromanyetik ortamlarda nanolif üretimi gerçekleir.

PVA SLIME YAPIMI
lem çok basit iki aamadan oluur. Sadece sizi uratracak ksm PVA çözdürme ilemidir. Onu da bir gün önceden aada belirtilen oranlarda slatma ilemi yapp ertesi gün kartrma ilemine geçerseniz daha kolay hale getirirsiniz.
1. 1 su barda (150 ml) scak su (yaklak 70 °C ) içerisinde 3 çay ka ( 6 gram) PVA iyice kartrlarak çözdürülür. Bu ilem biraz zaman alr. Önce PVA y bu suda bekletip biraz kartrdak sonra gün ar hidratlamas için bekleyebilirsiniz. Ertesi gün PVA l suyu tekrar stp kartrma ilemine berrak çözelti elde edene kadar devam edebilirsiniz.
2. yarm çay barda (37,5 ml) normal scaklktaki su içerisinde 1 çay kandan biraz az ( 1,5 gram) boraks (borax) kartrlarak çözdürülür.
3. Daha sonra 1 Su barda PVA solüsyonu ile yarm çay barda Boraks solüsyonu ayr bir kapta birletirilir ve güzelce kartrlr. Zaten hemen yap kazanp slime halini alacaktr.
PVA 2488 is raw materials of vinylon fibers,construction,paint additives, mainly used in textile,fabric finishing agents

PVA 2499 is mainly used as a warp dressing agent; textile finishing agent and the raw material of vinylon in textile industry; used a s 107/801 glue, an additive of cement and mortar, inner and outer wall paints, and mounding board binder in construction upholstery industry; used as a well-fixing agent in petroleum exploitation; used in cosmetic, printing, medicine and electronic, also can be used in chemical industry, paper industry and agriculture, etc.
Polivinil alkol (PVAL, PVA, PVOH), çounlukla polivinil asetatn (PVAC) sabunlatrlmas (hidrolizi) ile üretilen, sarms bir toz halinde termoplastik bir malzemedir. Dorudan sentetik yol mümkün deildir. PVAL hemen hemen bütün susuz organik çözücülere kar dirençlidir. Ksmen sabunlatrlm PVAL kaliteleri yakl. % 13 PVAC içerii ile suda kolayca çözünür. Sabunlama derecesi arttkça, sudaki çözünürlük azalr.

PVA ‘nn özellikleri
Yüksek çekme dayanm
Esneklik
Su emici
Yalara ve organik çözücülere kar dayankl
PVA ‘nn kullanm alanlar
Kat üretim ve ileme, kontraplak, sanat levha ve ahap ileme, emülsifiye edici ve dengeleyici maddeler, inaat endüstrisi, PVA filmi, bask ve tekstil
Dier reçinelerin hazrl için bir balangç maddesi olarak kullanlr. Süngerlerin üretiminde kullanlan elastomerlerin bir komponenti olarak kullanlabilir. Bu polimer kat veya tekstiller üzerinde yalar ve makine yalarna dayankllk veren aharlama ajanlar olarak kullanlrlar, filmleri solventler veya oksijen tarafndan saldrya dayankl yapmak için kullanlr. Polivinil alkol ayrca yaptrclarn, emülsifiyerlerin, süspanse edici ve klnlatrc (kvam verici) ajanlarn bir komponenti olarak kullanlabilir. laç endüstrisinde, polivinil alkol optalmik yalayc ve viskosite artrc ajan olarak kullanlmaktadr. Polivinil alkol, gözlerdeki göz yann doal filmini kalnlatrr.
Yara iyilemesi birçok hücre tipleri, büyüme faktörleri ve 1-3 bileikleri içeren karmak, çok aamal bir süreçtir. In vivo olarak yürütülen zaman Çünkü bu karmaklk, yara iyilemesi çalmalar en kapsaml vardr. In vivo insizyonel, eksizyonel, ölü boluk dahil olmak üzere akut yara iyilemesi, çalma mevcut modeller, ve yank birçok vardr. Ölü boluk modelleri yara dokusu oluumu ve maddelerin etkilerini incelemek amacyla kullanlan yapay gözenekli implantlar vardr. Yaygn olarak kullanlan ölü boluk Baz modellerin polivinil alkol (PVA) süngerler, çelik hasr silindir, geniletilmi politetrafloroetilen (ePTFE) malzeme ve Cellstick 1,2 içerir.

Her ölü alan model, malzemenin kompozisyonu ve implantasyon yöntemlerine dayal kendi snrlamalar vardr. Çelik hasr silindirli model implantasyonu sonras infiltrasyon bir lag faz vardr ve granülasyon dokusu oluumu Begi önce uzun bir zaman gerektirirns 1. Yara iyilemesi ileriki aamalarnda en iyi ePTFE modeli 1,4 kullanlarak analiz edilmektedir. Cellstick tipik insan ameliyat yaralar çalmak için kullanlan ve akkan 2 sarlr bir silikon tüp model içinde bir selüloz sünger. Süresi ile 5 hayvan dev bir hücre reaksiyonu neden olan bir yabanc cisimlerin tepkisi provoke balar, çünkü PVA sünger, akut çalmalar ile snrldr. Dier malzemelerin aksine, PVA sünger takmak ve çkarmak, inert ve biyolojik malzemelerden yaplan ve henüz histolojik analiz için 2,5 kesitli olmak için yeterince yumuak kolaydr.

Yara olarak PVA sünger ifa granülasyon dokusu oluumu analiz etmek için çok yararldr, kollajen depolanmas, yara svs kompozisyon ve iyileme süreci 1,2,5, kimyasal maddelerin etkileri. Yara iyilemesi niteliklerini geni bir dizi okuyan içinde kullanm yan sra, PVA sünger, ayn zamanda çalmalar dier birçok türde kullanlmtr. Bu holarak tümör anjiyogenezi, ilaç datm ve kök hücre sakalm ve engraftman 1,2,6,7 aratrmak için kullanlmtr. Onun büyük alterability, önceden yaygn olarak kullanlmas ve tekrarlanabilir sonuçlar ile, PVA sünger pek çok çalmada 1,2 için ideal bir modeldir.
Poli (vinil alkol) ( PVOH , PVA veya PVAl ) suda çözünebilen bir sentetik polimerdir. deal hale getirilmi formülü [CH2CH (OH)] n’dir. Kat yapmnda, tekstilde ve çeitli kaplamalarda kullanlr. Beyaz (renksiz) ve kokusuzdur. Bazen boncuk olarak veya suda çözelti olarak tedarik edilir.
Her iki poval. Vinil alkolün bir polimerine karlk gelen bir polimer bileimi. Genellikle vinil asetatn kostik ile hidrolize edilmesiyle elde edilir. Renksiz effaf. Suda çözünür filmler için dorudan kullanlr, dokuma kuma terbiye, yaptrclar, emülgatörler ve benzerleri için macun kullanlr, ancak bunlarn çou sentetik fiber vinil için hammaddelerdir.
Poli (vinil alkol) ( PVOH , PVA ya da PVAL ) a, suda – çözünebilir sentetik polimer . Bu idealize formül [CH sahip 2 -CH (OH)] n . Bu kullanlan kat yapm , tekstil atlama boyutlandrma , bir kalnlatrc ve emülsiyon stabilize edici madde olarak, PVAc yaptrc formülasyonlar ve kaplamalar çeitli. Renksiz (beyaz) ve kokusuzdur. Genellikle boncuk veya suda çözelti olarak salanr.
PVA, biyouyumluluu, düük protein yapmas eilimi ve düük toksisitesi nedeniyle çeitli tbbi uygulamalarda kullanlmaktadr. Belirli kullanmlar arasnda kkrdak replasmanlar, kontakt lensler ve göz damlalar bulunur . [5] Polivinil alkol, süspansiyon polimerizasyonlarnda yardmc olarak kullanlr . Çin’deki en büyük uygulamas, polivinil asetat dispersiyonlar yapmak için koruyucu bir kolloid olarak kullanlmasdr . Japonya’da ana kullanm Vinylon elyaf üretimidir . [6] Bu elyaf, kendi kendine yeterlilik nedenleriyle Kuzey Kore’de de üretilmektedir , çünkü onu üretmek için ya gerekmemektedir. Dier bir uygulama ise fotoraf filmidir.[7]

Tbbi olarak, bir Uterin Fibroid Embolektomisinde (UFE) embolik ajan olarak da kullanlabilir [8]

Polivinil asetaller
Polivinil asetaller , PVA’nn aldehitlerle ilenmesiyle hazrlanr . Butiraldehit ve formaldehit elde polivinil butiral (PVB) ve polivinil formal , srasyla, (PVF). Polivinil bütiralin hazrlanmas, ABD ve Bat Avrupa’da polivinil alkol için en büyük kullanmdr.

Hazrlk
Çou vinil polimerden farkl olarak , PVA, monomer, vinil alkol , tautomer asetaldehite göre termodinamik olarak kararsz olduundan , karlk gelen monomerin polimerizasyonu ile hazrlanmaz . Bunun yerine, PVA, polivinil asetat [3] veya bazen asetat yerine format veya kloroasetat gruplar ile dier vinil ester türevli polimerlerin hidrolizi ile hazrlanr . Polivinil esterlerin dönüümü genellikle etanol ile baz katalizli transesterifikasyonla gerçekletirilir:

[CH 2 , CH (OAc)] n + C 2 H 5 OH → [CH 2 , CH (OH)] n + C 2 H 5 OAc
Polimerin özellikleri, transesterifikasyon derecesinden etkilenir.

2006 ylnda dünya çapnda polivinil alkol tüketimi bir milyon metrik tonun üzerindeydi. [6] Büyük üreticiler arasnda Kuraray (Japonya, Avrupa ve ABD) ve Sekisui Speciality Chemicals (ABD) yer alrken, Çin anakarasnda bir dizi çok büyük üretim tesisi kurmutur. son on ylda ve u anda dünya kapasitesinin% 45’ini oluturuyor.

Yap ve özellikler
PVA, kristallik gösteren ataktik bir malzemedir . Mikro açsndan, esas olarak 1,3-diol balar olumaktadr [-CH 2 -CH (OH) -CH 2 -CH (OH) -], ancak 1,2-diollerin [CH birkaç yüzde 2 – CH (OH) -CH (OH) -CH 2 -] vinil ester balangç maddesinin polimerizasyonu için koullara bal olarak ortaya çkar. [3]

Polivinil alkol, mükemmel film oluturucu, emülsifiye edici ve yapkan özelliklere sahiptir. Ayrca ya, gres ve çözücülere kar dayankldr . Yüksek çekme mukavemeti ve esnekliinin yan sra yüksek oksijen ve aroma bariyer özelliklerine sahiptir. Bununla birlikte, bu özellikler neme baldr : daha yüksek nem seviyelerinde emilen su, polimerin gerilme mukavemetini azaltan, ancak uzama ve yrtlma mukavemetini artran bir plastikletirici görevi görür.

Güvenlik ve çevresel hususlar
PVA yaygn olarak kullanlmaktadr, bu nedenle toksisitesi ve biyolojik bozunmas ilgi çekicidir. % 5’e kadar PVA içeren solüsyonlar balklar için toksik deildir. [3] Yava biyolojik bozunur.
Monomer birimlerinden balayarak polimer birimlerinin elde edilmesine yol açan reaksiyonlara polimerizasyon reaksiyonlar denir. Polimerizasyon reaksiyonlar temelde iki türlü olabilir.

Step-Reaction (younlama)
Chain-Reaction (zincir reaksiyonu)
Örnek: Polivinil alkol ve gelatin, pektine ilave edildiinde hidroksil gruplar pektin zincirindeki -O atomlar ve -OH gruplar ile zincir yapar

Polimerizasyon bir mürekkep kurutma eklidir;

b) Kimyevi kuruma

– Polimerizasyon
– Polikondenzasyon
– Oksijenle birleme (Oksidativ kuruma) Kâdn yaps, kâdn yüzeyi, kâdn asit
durumu (pH), atölyenin scakl, segatif miktar, mürekkebin yaps ve pigment alabilme kabiliyeti Kurumaya dorudan ya da dolayl olarak etki eden faktörlerdir. Her mürekkebe az da olsa bir miktar segatif konur. Segatifler mürekkebin yapma hassasiyetini azaltr ve ayrlma özelliini arttrr. Yani içinde segatif olan mürekkepler, daha çabuk kurur, daha az yapr ve daha çok yaylr. Baz mürekkepler, içlerinde yeterli segatif olduu halde, nemleri fazla olduundan geç kururlar. Bazlar ise nem miktar artt halde fazla segatife ihtiyaç göstermezler. Esas “Baz” olan pigmentler, esas “Asit” olan pigmentlere oranla daha çabuk kururlar. Sonuç olarak her cins mürekkep ve renkte deiik bir kuruma hassasiyeti vardr. Ayrca iyi kuruyan bir mürekkep, üst üste iki defa basldnda, ikincisi birincisinde olduu gibi ayn hzda kurumaz.
poliol çoklu hidroksil gruplarn içeren bir organik bileik’tir. “Poliol” teriminin gda bilimi ile polimer kimyasnda kullanmlarnda farkl anlamlar olabilir. ki hidroksil grubundan daha fazlasna sahip olan molekül polioldur, üç tanelisi – triol ve dörtlüsü – tetroldür. Geleneksel olarak polioller dier fonksiyonel gruplar içeren bileikleri ifade etmezler.
snflandrma
Düük moleküler arlkl polioller
Düük moleküler arlkl poliol örnekleri
Pentaerythritol.svg
Pentaerythritol
Xylitol Structural Formula V.1.svg
Xylitol

eker alkolleri
Polioller snfnn birisi olan eker alkolleri genellikle ekerlerin hidrojenasyonu ile elde edilirler. Formülü (CHOH)nH2 dür burada n = 4-6‘dr.[1]

ekerlerden daha az kalori içerdiklerinden eker alkolleri gdalara konulur; ancak genelde daha az tatldrlar ve sklkla çok iddetli tatlandrclarla birletirilirler. Sakza da eklenirler çünkü azda bakterilerle parçalanmazlar ya da asitlere metabolize olmazlar böylece di çürümesine neden olmazlar. Maltitol, sorbitol, xylitol, erythritol ve isomalt yaygn eker alkolleridir.

Polimerik polioller
Polimerik poliol örnekleri
Polyether Polyol Structural Formula V3.svg
polieter poliol

(eter gruplarnn oksijen atomlar mavi renkle gösterilmitir.)

Polyester Polyol Structural Formula V.3.svg
polyester poliol
(ester gruplarnn oksijen ve karbon atomlar maviyle gösterilmitir.)

Poliol terimi poliol polieterleri ve polyesterler (“polieter poliolleri” ve “polyester poliolleri”) için kullanlr. Tipik örnei, polietilen oksit ya da polietilen glikol (PEG) ve polipropilen glikol (PPG)‘dir. Poliol, poliüretan üretiminde diizosiyanat’larla birleiminde monomer olarak kullanlr.

“Poliol” ifadesi çok sayda hidroksil grubu içeren polimerlere örnein polivinil alkol (CH2CHOH)n formülüne sahiptir yani n’nin binlerde olabilecei n alkol grubuna sahiptir. Selüloz poliol pek çok alkol grubuna sahip bir polimerdir ancak genellikle poliol olarak adlandrlmaz.

Terminal hidroksil gruplar içeren polimerik bileikler (polieter polioller ve polyester polioller) ile çoklu hidroksil gruplar içeren polimerik bileikler (örnein polivinil alkol) arasnda bir ayrm yaplmaldr.

Kullanm
Polimerik polioller
Polimerik polioller yatak, buzdolab ve dondurucu için köpük yaltm, ev ve otomotiv koltuklar poliüretanlar, elastomerik ayakkab tabanlar, elyaflar (örnein Spandex) ve yaptrc yapmak için izosiyanatlar ile reaksiyona girerler.
Düük molekül arlkl polioller
Poliol gliserol (krmz, düük molekül arlkl poliol) ve fitalik anhidrid’den türetilen ideal alkid reçine’nin yaps.
Düük molekül arlkl polioller, çapraz balama maddeleri olarak ilev gördükleri polimer kimyas’nda yaygn olarak kullanlr. Alkid reçineleri boyalarda ve döküm kalplarnda kullanlr. Çou ticari “ya bazl” kaplamada baskn reçine veya “balayc” dr. Her yl yaklak 200,000 ton alkid reçinesi üretilir. Reaktif monomerlerin ester oluumu ile balanmasna dayanrlar. Ticari alkid reçinelerinin üretiminde kullanlan polioller, gliserol, trimetilolpropan ve pentaeritritoldür.

Nanobilim
Metal nanoparçacklarn hazrlanmasnda genellikle “poliol yöntemi” kullanlr. Bu gibi durumlarda, poliol genellikle heksadekanediol ((CH2)16(OH)2) gibi uzun zincirli bir dioldür. Bu tür dioller, nanoparçacklar için hem indirgeyici hem de yüzey koruyucu ajanlar olarak ilev görür.

Özellikler
Poliol genel terimi sadece kimyasal adlandrma ‘dan türetildiinden ve sadece birkaç hidroksil grubunun varln gösterdiinden tüm poliollere ortak bir özellik atanamaz. Bununla birlikte, polioller oda scaklnda genellikle katya yakn derecede (düük molekül arlkl olduunda) oldukça yapkandrlar(polimerik olduunda). Bunun nedeni ayr ayr moleküller arasnda hidrojen ba olumasdr.
Poli (vinil alkol) suda çözünebilen, renksiz ve kokusuz sentetik bir polimerdir. Kimyasal formülü [CH2CH(OH)]n dir. Bazen boncuk formunda bazende su içinde çözelti halindedir.

Saf sulu çözeltilerde nötr yada hafif asidiktir ve küf oluumu gösterebilir. pH derecesi 5-8. Güçlü bir hidrofiliktir.

PVA, polivinil asetatn hidroliz edilmesiyle elde edilir. Poliesterlerin çevrilmesi sklkla etil alkol ile bir baz katalizörlüünde transesterifikasyon ile meydan gelir:

[CH2CH (OAc)]n + C2H5OH → [CH2CH(OH)]n + C2H5OAc

Polimerin özellikleri transesterifikasyon derecesine göre deiiklik gösterir.

Polivinil asetatlardan elde edilen bir polimer, asetat gruplarnn hidroksil gruplaryla yer deitirilmesi sonucunda elde edilir. Farmasötik süngerler ve oftalmik yalayc gibi suni süngerler, kozmetikler ve dier ürünlerin yüzey kaplamalarnn imalatnda kullanlr.Kat yapmnda, tekstilde ve çeitli kaplamalarda kullanlr.

Plastik endüstrisinde kalplama bileikleri, yüzey kaplamalar, benzine dirençli filmler, tekstil ebatlar ve terbiye bileimleri; suni süngerlerin, yakt hortumlarnn. imalatnda, ayrca plastik ve cam bask mürekkeplerinde, kozmetikte, suda çözünür film ve kaplamada kullanlacak elastomerler verecek ekilde PVA ile birletirilebilir. Farmasötik endüstride viskozite arttrc ajan olarak kullanlmaktadr.

Tp alannda da yaygn olarak kullanlmaktadr. Katyonik polivinil alkol hidrojel, kkrdak protezlerini yalamak için hazrlanr. PVA ayrca, elektron n altnda sulu çözücü içerisinde tamamen hidrolize edilmi kaliteyi çapraz balayarak sentetik kkrdak olarak kullanm için aratrmalar yaplmtr. Pva sünger protez meme implant olarakta kullanlmtr.

PVA’nn kimyasal ve fiziksel özellikleri geni bir kullanm alanna sahiptir: tekstil alannda , yaptrclarda ve polimerizasyon stabilizatörlerinde de uygulama alan vardr.
polivinil alkol moleküler formül (C) ‘nin vinil alkolünün bir polimeridir2’H3OR) n, burada R, H veya COCH’yi temsil eder3. Vinil alkolün dengesizlii nedeniyle, meneli polivinil asetatn polimerlemesini salayan bir monomer olarak vinil asetat kullanlarak sentezlenir..
Polivinil alkol yaps, özellikleri, kullanm alanlar, riskleri

polivinil alkol moleküler formül (C) ‘nin vinil alkolünün bir polimeridir2’H3OR) n, burada R, H veya COCH’yi temsil eder3. Vinil alkolün dengesizlii nedeniyle, meneli polivinil asetatn polimerlemesini salayan bir monomer olarak vinil asetat kullanlarak sentezlenir..

Daha sonra, sodyum hidroksit varlnda, polivinil asetat esterlerinin bir hidrolizi vardr, asetat yerine oksihidrit grubu (OH) geçerek polivinil alkolü oluturur. Bu esas olarak 1-3 diol bandan oluur [-CH2-CH (OH) -CH2-CH (OH) -].

Bu alkol, güçlü gerilmelere dayanabilen, emülsiyon oluturma ve yaptrma kapasitesine sahip filmler oluturabilir. Esnek bir malzeme olmasnn yan sra, polivinil alkol higroskopiktir ve suda çok çözünür, özellikleri hidrasyon derecesinden etkilenir..

lk olarak, 1924’te Hermann ve Haehnel tarafndan hazrland, etanol varlnda potasyum hidroksit ile polivinil asetatn hidrolize edilmesi.
Polivinil alkol, oksijen ve aromalara engel olan tabakalarn veya filmlerin imalatnda kullanlabilir. Bu, gda ambalajlarnda kullanlmasna izin verdi, bunun ana kullanmyd, çünkü üretiminin% 30’undan fazlas bu amaç için kullanlyor.
Tüm balantlarn basit olduunu ve bu nedenle karbonlarn ve oksijenin, hibridizasyona sahip olduunu unutmayn.3. Bu ne anlama geliyor? Polivinil alkolün zincirlerinin düz olmadklarn, zikzakl olduklarn ve H’nin atomlarnn yanlarna döndüklerini söylemesi. Ayn OH hidroksil gruplar için de geçerli.
olivinil alkol, su molekülleri ve hidrojen balaryla etkileime girebilecei dier çözücüler için özel bir afiniteye sahip olan basit ancak dinamik ve polar bir polimer yapsna sahip olabilir: CH (O-H) – OH2.

özellikleri
Fiziksel açklama
Kokusuz beyaz krem, granül veya tozu
Kaynama noktas
644º F ila 760 mmHg (yaklak olarak).

Erime noktas
442º F (ayrma yaar).
Ateleme noktas
175º F (79º C) açk kap.
Suda çözünürlük
Polimerin moleküler arln azaltarak çözünürlüü artrarak çözülebilir.
çözünürlük
Etanolde çözünür, fakat dier organik çözücülerde çözünmez. Petroldeki solventlerde çözünmez. Bitkisel ve hayvansal yalarda, aromatik hidrokarbonlarda, esterlerde, eterlerde ve asetonda pratik olarak çözünmez.

younluk
1,19 – 1,31 g / cm3.

Buhar basnc
kararllk
Depolama koullarnn önerilmesi kararldr..
ayrma
200 ºC’ye kadar stldnda, keskin ve tahri edici bir duman yayarak ayrr..

Viskozite:
4,8 ila 5,8 mPa arasnda (ortalama 26,000 ila 30,000 g / mol moleküler arla karlk gelen 20 ° C’de% 4 çözelti).

Polivinil alkolün viskozitesine göre farkl dereceleri vardr: süper yüksek (moleküler arlk 250.000 – 300000 g / mol), yüksek viskozite (moleküler arlk 170.000 – 220.000 g / mol, ortalama viskozite (moleküler arlk 120.000 – 150.000 g / mol) ve viskozite düük (moleküler arlk 25.000 – 35.000 g / mol).

Polivinil alkolün viskozitesi ile molekül arl arasnda dorudan orantllk vardr..

pH: 5.0 – 6.5 (% 4 çözelti).
uygulamalar
sentetikler
-Polivinil nitrat, nitrik asit esteri ve polivinil alkol gibi dier polimerlerin sentezi için bir malzemedir. Polivinil nitrat baz itici gazlarda ve kalplanabilir patlayclarda kullanlr.
Lifler ve levhalar
-Polivinil alkol lifleri, dier liflerden% 30 daha yüksek bir su emme kapasitesine sahiptir. Bu, elyafn vücutla temas ettii yerlerde kullanlan pamuu deitirmenize olanak salar. Polivinil alkolden yaplm kuman dokunsal hissi, yün öncesi yaanandan nevresimden önceki benzerine kadar deiebilir..
-Polivinil alkollü tabakalar gda ambalajlarnda kullanlr, çünkü oksijen ve aromalara kar bir engel görevi görebilir. Bu, gdann oksidasyona uramasn ve lezzetini kaybetmesini önler. Buna ek olarak, dardaki kokularn yemein orijinal tadna müdahale etmesini önler.
-Polivinil asetat yapkann kalnlatrmak ve deitirmek için kullanlr. Çamarlarda polivinil alkollü tabakalarla yaplm zarflarda deterjan salnmn dozlamak için kullanlr.
-Kadn hijyeninin yan sra idrar kaçrma için havlular, biyobozunur polivinil alkol filminden yaplm torbalarla paketlenmitir. Biyolojik örneklerin, özellikle dk örneklerinin toplanmasnda fiksatif olarak kullanlr.
Seryum iyonuyla oksidasyonun en önemli özellii, elektron transferinin indirgenen ajan üzerinde gerçekleerek serbest radikaller oluturmasdr. Böylelikle, eer indirgeme ajan niasta, selüloz veya polivinil alkol gibi polimerik bir madde ise ve oksidasyon vinil monomerinin varlnda gerçekleiyorsa, polimer ana zinciri üzerinde graft kopolimerler oluturan serbest radikaller meydana gelir. Bu metod, ana zincir üzerinde yeterli sayda serbest radikal oluturduu için elde edilen graft kopolimer verimi oldukça yüksektir. Dier bir avantaj ise reaksiyonun oda scaklnda kolaylkla yaplabilmesidir.
Bunlarn haricinde, polivinilalkol, polietilen oksit ve N-vinil pirolidon gibi hidrofilik polimerler de çözünmeyi önlemek için çapraz balar oluturulduktan sonra, su absorban polimerler olarak kullanlrlar [36]. Son yllarda, su absorban polimerler üzerindeki çalmalarda önemli miktarda art gözlenmitir. Niasta-graft kopolimerler, bu çalmalar içerisinde önemli bir yüzdeye sahiptir.